To improve oil recovery significantly in low-mid permeability reservoirs, a novel modified nano-SiO₂ hyperbranched copolymer (HPBS), consisting of polyacrylamide as hydrophilic branched chains and modified nano-SiO₂ as the core, was synthesized via an in situ free radical polymerization reaction. The structure and properties of the hyperbranched copolymer were characterized through a range of experiments, which showed that HBPS copolymers have better stability and enhanced oil recovery (EOR) capacity and also smaller hydrodynamic radius in comparison with hydrolyzed polyacrylamide (HPAM). The flooding experiments indicated that when a 1000 mg/L HPBS solution was injected, the resistance factor (RF) and residual resistance factor (RRF) increased after the injection. Following a 98% water cut after preliminary water flooding, 0.3 pore volume (PV) and 1000 mg/L HPBS solution flooding and extended water flooding (EWF) can further increase the oil recovery by 18.74% in comparison with 8.12% oil recovery when using HPAM. In this study, one can recognize that polymer flooding would be applicable in low-mid permeability reservoirs.

A new type of chitosan-modified hyperbranched polymer (named HPDACS) was synthesized through the free-radical polymerization of surface-modified chitosan with acrylic acid (AA) and acrylamide (AM) to achieve an enhanced oil recovery. The optimal polymerization conditions of HPDACS were explored and its structure was characterized by Fourier-transform infrared spectroscopy, hydrogen nuclear magnetic resonance, and environmental scanning electron microscopy. The solution properties of HPDACS in ultrapure water and simulated brine were deeply studied and then compared with those of partially hydrolyzed polyacrylamide (HPAM) and a dendritic polymer named HPDA. The experimental results showed that HPDACS has a good thickening ability, temperature resistance, and salt resistance. Its viscosity retention rate exceeded 79.49% after 90 days of aging, thus meeting the performance requirements of polymer flooding. After mechanical shearing, the viscosity retention rates of HPDACS in ultrapure water and simulated brine were higher than those of HPAM and HPDA, indicating its excellent shear resistance and good viscoelasticity. Following a 95% water cut after preliminary water flooding, 0.3 pore volume (PV) and 1500 mg/L HPDACS solution flooding and extended water flooding could further increase the oil recovery by 19.20%, which was higher than that by HPAM at 10.65% and HPDA at 13.72%. This finding indicates that HPDACS has great potential for oil displacement.

Effects of fracturing fluid composition and other factors on improving the oil imbibition recovery of shale reservoir