The characteristics of magnetostructural coupling play a crucial role in the magnetic field-driven behaviour of magnetofunctional alloys. The availability of magnetostructural coupling over a broad temperature range is of great significance for scientific and technological purposes. This work demonstrates that strong magnetostrucural coupling can be achieved over a wide temperature range (222 to 355 K) in Co-doped high Mn-content Mn₅₀Ni_42−x Co _x Sn₈ (0 ≤ x ≤ 10) melt-spun ribbons. It is shown that, over a wide composition range with Co content from 3 to 9 at.%, the paramagnetic austenite first transforms into ferromagnetic austenite at T _C on cooling, then the ferromagnetic austenite further transforms into a weakly magnetic martensite at T _M. Such strong magnetostructural coupling enables the ribbons to exhibit field-induced inverse martensitic transformation behaviour and a large magnetocaloric effect. Under a field change of 5 T, a maximum magnetic entropy change ΔS _M of 18.6 J kg⁻¹ K⁻¹ and an effective refrigerant capacity RC _eff of up to 178 J kg⁻¹ can be achieved, which are comparable with or even superior to those of Ni-rich Ni–Mn-based polycrystalline bulk alloys. The combination of high performance and low cost makes Mn–Ni–Co–Sn ribbons of great interest as potential candidates for magnetic refrigeration.

Reconstructive phase transitions involving breaking and reconstruction of primary chemical bonds are ubiquitous and important for many technological applications. In contrast to displacive phase transitions, the dynamics of reconstructive phase transitions are usually slow due to the large energy barrier. Nevertheless, the reconstructive phase transformation from β- to λ-Ti₃O₅ exhibits an ultrafast and reversible behavior. Despite extensive studies, the underlying microscopic mechanism remains unclear. Here, we discover a kinetically favorable in-plane nucleated layer-by-layer transformation mechanism through metadynamics and large-scale molecular dynamics simulations. This is enabled by developing an efficient machine learning potential with near first-principles accuracy through an on-the-fly active learning method and an advanced sampling technique. Our results reveal that the β−λ phase transformation initiates with the formation of two-dimensional nuclei in the a b-plane and then proceeds layer-by-layer through a multistep barrier-lowering kinetic process via intermediate metastable phases. Our work not only provides important insight into the ultrafast and reversible nature of the β−λ transition, but also presents useful strategies and methods for tackling other complex structural phase transitions.

Heusler type Ni-Mn-Ga ferromagnetic shape memory alloys can demonstrate excellent magnetic shape memory effect in single crystals. However, such effect in polycrystalline alloys is greatly weakened due to the random distribution of crystallographic orientation. Microstructure optimization and texture control are of great significance and challenge to improve the functional behaviors of polycrystalline alloys. In this paper, we summarize our recent progress on the microstructure control in polycrystalline Ni-Mn-Ga alloys in the form of bulk alloys, melt-spun ribbons and thin films, based on the detailed crystallographic characterizations through neutron diffraction, X-ray diffraction and electron backscatter diffraction. The presented results are expected to offer some guidelines for the microstructure modification and functional performance control of ferromagnetic shape memory alloys.

For Heusler-type Ni–Mn–Ga ferromagnetic shape-memory alloys, the configuration of the martensite variants is a decisive factor in achieving a large magnetic shape-memory effect through field-induced variant reorientation. Based upon the spatially resolved electron backscatter diffraction technique, the microstructural evolution associated with the martensitic transformation from austenite to seven-layered modulated (7M) martensite was investigated on a polycrystalline Ni₅₃Mn₂₂Ga₂₅alloy. It was clearly shown that grain interior nucleation led to the formation of diamond-shaped 7M martensite within the parent austenite matrix. This diamond microstructure underwent further growth through an isotropic expansion with the coordinated outward movement of four side habit planes, followed by an anisotropic elongation with the forward extension of a type-I twin pair. A two-step growth model is proposed to describe the specific morphology and crystallography of 7M martensite. In addition, the habit planes were revealed to possess a stepped structure, with the {1 0 1}_Aplane as the terrace and the {0 1 0}_Aplane as the step. The characteristic combination of martensite variants and the underlying mechanism of self-accommodation in the martensitic transformation have been analysed in terms of the minimum total transformation strain, where the deformation gradient matrix was constructed according to the experimentally determined orientation relationship between the two phases. The present results may deepen the understanding of special martensite microstructures during the martensitic transformation in ferromagnetic shape-memory alloys.