Chitin nanofibers sheets (CNFSs) with nanoscale fiber-like surface structures are nontoxic and biodegradable biomaterials with large surface-to-mass ratio. CNFSs are widely applied as biomedical materials such as a functional wound dressing. This study aimed to develop antimicrobial biomaterials made up of CNFS-immobilized silver nanoparticles (CNFS/Ag NPs). CNFSs were immersed in suspensions of Ag NPs (5.17 ± 1.9 nm in diameter; mean ± SD) for 30 min at room temperature to produce CNFS/Ag NPs. CNFS/Ag NPs were characterized by transmission electron microscopy (TEM) and then tested for antimicrobial activities against Escherichia (E.) coli, Pseudomonas (P.) aeruginosa, and H1N1 influenza A virus, three pathogens that represent the most widespread infectious bacteria and viruses. Ultrathin sectioning of bacterial cells also was carried out to observe the bactericidal mechanism of Ag NPs. The TEM images indicated that the Ag NPs are dispersed and tightly adsorbed onto CNFSs. Although CNFSs alone have only weak antimicrobial activity, CNFS/Ag NPs showed much stronger antimicrobial properties against E. coli, P. aeruginosa, and influenza A virus, with the amount of immobilized Ag NPs onto CNFSs. Our results suggest that CNFS/Ag NPs interacting with those microbes exhibit stronger antimicrobial activities, and that it is possible to apply CNFS/Ag NPs as anti-virus sheets as well as anti-infectious wound dressings.

Size-controlled spherical silver nanoparticles (<10 nm) and chitin-nanofiber sheet composites (Ag NPs/CNFS) have previously been reported to have strong antimicrobial activity in vitro. Although Ag NPs/CNFS have strong antimicrobial activity, their cytotoxicity has not been investigated. This study was performed to evaluate the effects of Ag NPs/CNFS on cytotoxicity for fibroblasts in vitro and healing delay of wound repair in vivo, focused on oxidative stress. Cytotoxic activities of Ag NPs/CNFS were investigated using a fibroblast cell proliferation assay, nitric oxide/nitrogen dioxide (NO/NO₂) measurement of the cell lysates in vitro, inhibitory effects of Ag NPs/CNFS on healing-impaired wound repair using diabetic mice in vivo, 8-hydroxy-2′-deoxyguanosine (8-OHdG) immunohistochemical staining of the skin sections, and generation of carbonyl protein in the wound was performed to evaluate cytotoxicity with oxidative stress. Ag NPs/CNFS exhibited cytotoxicity for fibroblasts and a significant increase of total NO/NO₂ levels in the cell lysates in vitro and increased levels of 8-OHdG and carbonyl proteins in vivo. Although wound repair in the continuously Ag NPs/CNFS-treated group was delayed, it could be mitigated by washing the covered wound with saline. Thus, Ag NPs/CNFS may become accepted as an anti-infectious wound dressing.