Water can trigger freeze–thaw cycles, acid rain corrosion, and microbial colonisation, all of which destroy stone. Water is one of the most influential factors in the destruction of outdoor stone heritage. Therefore, materials with excellent hydrophobic properties and durability are urgently required to effectively retard long-term stone weathering. In this study, two nanoparticles, TiO₂ and SiO₂, were used to modify dodecyltrimethoxysilane (DTMS), a waterproof coating commonly used for stone heritage protection, to fabricate nanocomposite superhydrophobic coatings. The micromorphology, water repellence (water contact angle and capillary water absorption), suitability to protect stone heritage (color change and water vapor permeability), and durability (thermal, light, and chemical stability) of DTMS and nanocomposite coatings were evaluated. The scanning electron microscope (SEM) images revealed that adding 0.5% (w/w) SiO₂ produced nanoscale roughness on the sandstone surface, leading to superhydrophobicity. The results of ultraviolet -visible (UV–Vis) spectrophotometer showed that adding 0.01% TiO₂ shielded more than 90% of UV light but accelerated the decrease in the contact angle under UVA irradiation. The addition of SiO₂ was able to avoid the detrimental effect of TiO₂ under UV light. The thermogravimetric analysis (TGA) results showed that both SiO₂ and TiO₂ nanoparticles improved the thermal stability of the coatings. In particular, the fabricated nanocomposite coating, SiO₂ and TiO₂ co-modified DTMS, had excellent water repellence, low color change and outstanding durability, and retained about 85% of the water vapor permeability of the stone, showing promise for stone protection.

Tomb No. 2 of Tushan in Xuzhou is the tomb of King Chu of the Eastern Han Dynasty, and it was an important archaeological discovery in China. The unique placement and crafting techniques of a lacquer coffin that was unearthed from the burial corridor are of significant importance in the study of tombs. In order to characterise the sample’s microstructure, elemental composition, and structural composition, as well as to study the crafting techniques of the coffin in the corridor, a range of analytical techniques were employed, including ultra-depth microscopy, scanning electron microscopy with SEM-EDS, Raman spectroscopy, FTIR, and XRD. The results indicate that the cross-sectional structure of the fragments comprises a pigment layer and a lacquer ash layer, with the latter being further divided into tile ash and bone ash layers. No lacquer film layer was observed. The primary colouring agent in the pigment layer was HgS, which contained a minor quantity of organic binder. The primary component of the tile ash layer was quartz, while the osseous ash layer comprised particles and collagen derived from mammalian bones. The lacquer crafting technique employed in the construction of the coffin was relatively simple and inconsistent with the assumption of it having a noble status. The findings of this research offer experimental data for the identification, preservation, and technical restoration of the corridor coffin in the future.

In the conservation of cultural relics, the application of Paraloid B72 in humid environments frequently results in the surface whitening of artifacts, which impairs their appearance and conceals important details. This study investigates the mechanisms underlying this phenomenon by examining the effect of ambient humidity, Paraloid B72 mass concentration, solution addition volume, and solvent type. To evaluate the microstructure, transmittance, and composition of the films, a range of analytical techniques were employed, including optical microscopy, scanning electron microscopy, a UV-Visible Spectrophotometer, and Fourier transform infrared spectroscopy. The findings indicate that higher ambient humidity, lower Paraloid B72 mass concentration, smaller solution addition volume, and solvents with higher volatility and water miscibility increase water content during curing, intensifying the whitening effect. These factors modify the interaction between water and solvent, altering the surface structure of Paraloid B72. The whitening mechanism is linked to the cooling effect of solvent volatility, which lowers the dew point temperature at the air–solution interface, causing moisture condensation. Moisture forms droplets that leave irregular pores upon volatility, resulting in surface roughness, optical heterogeneity, and a reduced refractive index, resulting in whitening. This study provides a theoretical basis for understanding and preventing the whitening of Paraloid B72.

Moisture-curable polyurethane (MCPU) is a specifically designed material for the consolidation of fragile cultural objects in high-humidity environments. In order to solve the problem of its susceptibility to yellowing due to heat ageing, polyhedral oligomeric silsesquioxane (POSS) was added to the MCPU to prepare POSS/MCPU. The appearance, stability and mechanical properties of the POSS/MCPU films were characterized using a UV–Vis spectrophotometer, a gloss meter, a colorimeter, a thermal analyzer and a universal material testing machine. The results showed that the films are colorless and transparent and have a light transmission of over 80%. The addition of POSS has almost no effect on the chromaticity of the MCPU, while the thermal stability of the POSS/MCPU is improved compared to the pristine MCPU. The modified film is 2.50 times more resistant to yellowing by heat. The addition of POSS also simultaneously enhances the strength and toughness of the film. Using POSS/MCPU to reinforce the fragile object, the material was found to be significantly effective, indicating it has the potential to be used during the extraction of fragile cultural objects from archaeological sites.