The modern concept of lightweight design (LW) requires the application of different materials in one structure (multi-material structures). The structure of different materials has a good perspective for application in the automotive and aerospace industries but only if it is possible to achieve a quality joint between different materials. The most used technology for joining different materials in the automotive industry is Resistance spot welding (RSW). Due to different mechanical, physical, and chemical properties, the joining of different materials by RSW technology does not provide a quality joint, and accordingly, alternative technologies for joining different materials have emerged. Resistance element welding (REW) was developed to enable joint of different materials. This paper presents the welding of AW 5754 H22 Al alloy (1.0 mm-thick) and DP500 steel (1.5 mm-thick) using novel REW. The peak load, absorption energy, microstructure, microhardness and fatigue strength of the REW joint has been investigated. The joint of the same materials has been done also using conventional RSW to compare some results. The results that will be presented in this paper show that that REW can achieve reliable joining of the two materials at relatively low welding currents compared to RSW. Using REW process with a significantly lower welding current, satisfactory mechanical characteristics of the weld joint can be achieved, so peak load is between 2300–2500 N, displacement is between 2.5–3 mm and the absorption energy is between 3.3–5.7 J. REW joints showed fatigue strength with the fatigue limit of 882 N.

In order to ensure a quality welded joint, and thus safe operation and high reliability of the welded part or structure achieved by friction stir welding, it is necessary to select the optimal welding parameters. The parameters of friction stir welding significantly affect the structure of the welded joint, and thus the mechanical properties of the welded joint. Investigation of the influence of friction stir welding parameters was performed on 6-mm thick plates of aluminum alloy AA2024 T351. The quality of the welded joint is predominantly influenced by the tool rotation speed n and the welding speed v. In this research, constant tool rotation speed was adopted n = 750 rpm, and the welding speed was varied (v = 73, 116 and 150 mm/min). By the visual method and radiographic examination, imperfections of the face and roots of the welded specimens were not found. This paper presents the performed experimental tests of the macro and microstructure of welded joints, followed by tests of micro hardness and fracture behavior of Friction Stir Welded AA2024-T351 joints. It can be concluded that the welding speed of v = 116 mm/min is favorable with regard to the fracture behavior of the analysed FSW-joint.

The aim of this work is to study joining Al 2024-T3 alloy plates with different welding procedures. Aluminum alloy AA 2024-T351 is especially used in the aerospace industry. Aluminum plates are welded by the TIG and MIG fusion welding process, as well as by the solid-state welding process, friction stir welding (FSW), which has recently become very important in aluminum and alloy welding. For welding AA2024-T35 with MIG and TIG fusion processes, the filler material ER 4043—AlSi₅ was chosen because of reduced cracking. Different methods were used to evaluate the quality of the produced joints, including macro- and microstructure evaluation, in addition to hardness and tensile tests. The ultimate tensile strength (UTS) of the FSW sample was found to be 80% higher than that of MIG and TIG samples. The average hardness value of the weld zone of metal for the MIG- and TIG-produced AA2024-T3511 butt joints showed a significant decrease compared to the hardness of the base metal AA2024-T351 by 50%, while for FSW joints, in the nugget zone, the hardness is about 10% lower relative to the base metal AA2024-T3511.

Adhesive bonding has proven to be a reliable method of joining materials, and the development of new adhesives has made it possible to use bonding in a variety of applications. This article addresses the challenges of bonding metals such as the aluminum alloy EN AW-5754 and the stainless steel X5CrNi18-10. In this study, the effects of laser cleaning and texturing on the surface properties and strength of two bonded joints were investigated and compared with mechanical preparation (hand sanding with Scotch-Brite and P180 sandpaper). The bonded joints were tested with three different epoxy adhesives. During the tests, the adhesion properties of the bonded surface were determined by measuring the contact angle and assessing the wettability, the surface roughness parameters for the different surface preparations, and the mechanical properties (tensile lap-shear strength). Based on the strength test results, it was found that bonded joints made of stainless steel had 16% to 40% higher strength than aluminum alloys when using the same adhesive and surface preparation. Laser cleaning resulted in maximum shear strength of the aluminum alloy bond, while the most suitable surface preparation for both materials was preparation with P180 sandpaper for all adhesives.

A threaded gear in machine tools is a mechanical actuator that converts rotary motion into linear one of the machine axis using a recirculating ball-nut. It provides positioning accuracy, uniform motion, silent operation, reduced wear and an increased service life. The bearing assembly of the threaded spindles should provide load transfer (cutting forces and friction forces) while maintaining high guiding accuracy. Due to a high number of the threaded spindle revolutions and the presence of tension in the bearing and a high axial force originating from the cutting and friction forces, the increased heat load due to friction in the bearings is normally expected. For this reason, this paper presents a thermal analysis of the bearing assembly of the threaded spindle which is realized via an axial ball bearing with angular contact of the ZKLN type, produced by the German manufacturer Schaeffler (INA); in other words, a numerical thermal analysis has been performed.