Natural fibers are one of effective substitute for switching artificial fiber and concentrating to reinforce polymer matrixes due to their decomposable character. This study was implied to realize physico-chemical properties of bio fiber obtained from Heteropogon contortus (HC) plant. Heteropogon contortus fibers (HCFs) had cellulose (64.87 wt. %), hemicellulose (19.34 wt. %), lignin (13.56 wt. %), and low density (602 kg/m³). The chemical functional group of HCFs was established by Fourier transform infrared spectroscopy, thermal stability of the fiber up to 220°C discovered by thermogravimetric analysis. Further the assets of HCFs proved that it can act as an excellent reinforcement material as a bio composite. Finally, the tensile properties were carried out through single fiber tensile tests, such as tensile strength, tensile modulus and microfibrillar angle.

Owing to their low weight-to-high strength ratio and recyclable features, the natural fibers are the most potential choice in place of synthetic fibers and been used as reinforcement materials in polymer matrix composites. Characterization of Ceiba pentandra bark fibers (CPFs) such chemical analysis, Fourier Transform-Infrared Analysis (FTIR), X-ray diffraction, thermogravimetric analysis, and Differential thermogravimetric analysis (DTG) analysis has analyzed. CPFs contain 60.9% (w/w) of cellulose, 17.5% (w/w) of hemicellulose, and 23.5% (w/w) of lignin. Besides, its density and crystallinity index are 682 kg m⁻³ and 57.94%, respectively. TG and DTG analysis discovered that CPFs are thermally stable up to 342.1°C. Further, all the resources of CPFs ensured that it can be an excellent alternative for synthetic fibers in polymer matrix composites.

Joining of dissimilar metals has various automotive, aerospace, nuclear, chemical, and cryogenic applications. The present study focuses on friction stud welding of aluminum and mild steel. Experiments had been conducted by varying the process parameters and the strength of the friction welded joints was evaluated. Experimental results show that the speed of rotation, friction time, and axial shortening distance have significant effect on the impact strength of the welded joints. The dissipation of frictional heat from the weld center results in temperature gradient across the welded joint, causing different zones with different microstructures. Scanning electron microscope (SEM) micrograph reveals the presence of three distinctive regions in the heat-affected zone, namely, fully plasticized deformed zone, partially deformed zone, and unaffected base metal zone. The microhardness values were measured across the welded joint. At the interfacial region, there is an increased plastic deformation. This is due to the rise in heat input during friction stage and applied upsetting load in the forging stage. Consequently, there is an increase in hardness at the interfacial region of the welded joint.