Etch pits could form on an exposed surface of a crystal when the crystal is exposed to an etching environment or chemicals. Due to different dissolution rates along various crystalline directions in a crystal, the dissolution process is anisotropic; hence, etch pits usually have a regular shape. Here, the morphology and origin of the regular-shaped etch pits are discussed firstly; then, factors which could affect the morphology and density of etch pits are shown; finally, the state of the art of etch pit technology and the utilization of etch pits is presented. Traditionally, etch pits are utilized to evaluate the dislocation density and some defect-related properties. Now, in the modern fabrication industries, the relationship between etch pits and defects has been utilized more skillfully. High-quality crystals can be fabricated by controlling dislocations revealed by etch pits. Meanwhile, with the as-revealed dislocation as the diffusion path of atoms, new crystals will emerge in corresponding etch pits.

Corrosion behavior of Mg‐5Y‐1.5Nd alloy was investigated after heat treatment. The microstructure and precipitation were studied by scanning electron microscope (SEM) and energy dispersive spectrometer (EDS). The weight loss rates of different samples were arranged as T6‐24 h>T6‐6 h>T6‐14 h>as‐cast>T4. The open circuit potential (OCP) showed that T4 sample had a more positive potential than that of other samples. The potentiodynamic polarization curves showed that the T6‐24 h sample had the highest corrosion current density of 245.362 μ A·cm ⁻² , whereas the T4 sample had the lowest at 52.164 μ A·cm ⁻² . The EIS results confirmed that the heat treatment reduced the corrosion resistance for Mg‐5Y‐1.5Nd alloy, because the precipitations acted as the cathode of electrochemical reactions to accelerate the corrosion process. The corrosion rates of different samples were mainly determined by the amount and distribution of the precipitations. The precipitations played dual roles that depended on the amount and distribution. The presence of the phase in the alloys could deteriorate the corrosion performance as it could act as an effective galvanic cathode. Otherwise, a fine and homogeneous phase appeared to be a better anticorrosion barrier.