A very simple, as well as sensitive and selective, sensing protocol was developed on a pre-anodized graphite pencil electrode surface coated using poly(thionine) (APGE/PTH). The poly(thionine) coated graphite pencil was then used for simultaneous sensing of 3-nitrophenol (3-NP) and 4-nitrophenol (4-NP). The poly(thionine) coated electrode exhibited an enhanced electrocatalytic property towards nitrophenol (3-NP and 4-NP) reduction. Redox peak potential and current of both nitrophenols were found well resolved and their simultaneous analysis was studied. Under optimized experimental conditions, APGE/PTH showed a long linear concentration range from 20 to 230 nM and 15 nM to 280 nM with a calculated limit of detection (LOD) of 4.5 and 4 nM and a sensitivity of 22.45 µA/nM and 27.12 µA/nM for 3-NP and 4-NP, respectively. Real sample analysis using the prepared sensor was tested with different environmental water samples and the sensors exhibited excellent recovery results in the range from 98.16 to 103.43%. Finally, the sensor exposed an promising selectivity, stability, and reproducibility towards sensing of 3-NP and 4-NP.

Biomass, though a major energy source, remains underutilized. Biochar from biomass pyrolysis, with its high porosity and surface area, is especially useful as catalyst support, enhancing catalytic activity and reducing electron recombination in photocatalysis. Indonesia, the world’s top palm oil producer, generated around 12 million tons of empty fruit bunches (EFBs) in 2023, making EFBs a promising biochar source. This study synthesizes biochar from leftover EFB fibers at 500, 800, and 1000 °C, analyzing structural changes via infrared and Raman spectroscopy, along with particle size and surface area analysis, laying the groundwork for future biochar research. The smallest particle size and highest surface area gained was 71.1 nm and 10.6 × 10² m²/g. Spectroscopic analysis indicates that biochar produced at 1000 °C has produced nano-crystalline graphite with a crystallite size of approximately 5.47 nm. This provides higher defect density, although with lower conductivity. Other studies indicate that our biochar can be used as catalyst support for various green energy-related applications, i.e., counter electrodes, electrocatalysts, and photocatalysts.

Water electrolysis is a highly efficient route to produce ideally clean H₂ fuel with excellent energy conversion efficiency and high gravimetric energy density, without producing carbon traces, unlike steam methane reforming, and it resolves the issues of environmental contamination via replacing the conventional fossil fuel. Particular importance lies in the advancement of highly effective non-precious catalysts for the oxygen evolution reaction (OER). The electrocatalytic activity of an active catalyst mainly depends on the material conductivity, accessible catalytically active sites, and intrinsic OER reaction kinetics, which can be tuned via introducing N heteroatoms in the catalyst structure. Herein, the efficacious nitrogenation of CuS was accomplished, synthesized using a hydrothermal procedure, and characterized for its electrocatalytic activity towards OER. The nitrogen-doped CuO@CuS (N,CuO@CuS) electrocatalyst exhibited superior OER activity compared to pristine CuS (268 and 602 mV), achieving a low overpotential of 240 and 392 mV at a current density of 10 and 100 mA/cm², respectively, ascribed to the favorable electronic structural modification triggered by nitrogen incorporation. The N,CuO@CuS also exhibits excellent endurance under varied current rates and a static potential response over 25 h with stability measured at 10 and 100 mA/cm².

Water electrolysis is a highly efficient route to produce ideally clean H2 fuel with excellent energy conversion efficiency and high gravimetric energy density, without producing carbon trace unlike steam methane reforming, and resolves the issues of environmental contamination via replacing the conventional fossil fuel. Of special importance lies in the advancement of highly effective non-precious catalysts for the oxygen evolution reaction (OER). The electrocatalytic activity of an active catalyst mainly depends on the material conductivity, accessible catalytically active sites, and intrinsic OER reaction kinetics, which can be tuned via introducing heteroatom N in the catalyst stricture. Herein, an efficacious nitrogenation of CuS has been accomplished, which was synthesized using hydrothermal procedure, and characterized for their electrocatalytic activity towards OER. The nitrogen-doped CuO@CuS (N,CuO@CuS) electrocatalyst exhibits superior OER activity than pristine CuS (268 and 602 mV), achieving the low overpotential of 240 and 392 mV at a current density of 10 and 100 mA/cm2, respectively, ascribed to the favorable electronic structural modification triggered by nitrogen incorporation. The N,CuO@CuS also exhibits excellent endurance under varied current rates and a static potential response over 25 h stability measured at 10 and 100 mA/cm2.