Purpose. To investigate the biomechanics of the anterior human corneal stroma using atomic force microscopy (AFM). Methods. AFM measurements were performed in liquid on the anterior stroma of human corneas, after gently removing the epithelium, using an atomic force microscope in the force spectroscopy mode. Rectangular silicon cantilevers with tip radius of 10 nm and spring elastic constants of 25- and 33-N/m were used. Each specimen was subjected to increasing loads up to a maximum of 2.7 μN with scan speeds ranging between 3- and 95-μm/s. The anterior stromal hysteresis during the extension–retraction cycle was quantified as a function of the application load and scan rate. The elastic modulus of the anterior stroma was determined by fitting force curve data to the Sneddon model. Results. The anterior stroma exhibited significant viscoelasticity at micrometric level: asymmetry in the curve loading–unloading response with considerable hysteresis dependent both on the application load and scan rate (P < 0.01). The mean elastic modulus ranged between 1.14 and 2.63 MPa and was constant over the range of indentation depths between 1.0 and 2.7 μm in the stroma. Conclusions. At microscale level, the mechanical response of the most anterior stroma is complex and nonlinear. The microstructure (fibers' packing, number of cross-links, water content) and the combination of elastic (collagen fibers) and viscous (matrix) components of the tissue influence the type of viscoelastic response. Efforts in modeling the biomechanics of human corneal tissue at micrometric level are needed.

To analyze intraocular lens (IOL) optic surface adhesiveness using atomic force microscopy (AFM). LiCryL Laboratory, University of Calabria, Rende, Italy. The surface adhesive properties of poly(methyl methacrylate) (PMMA), silicone, hydrophilic acrylic, and hydrophobic acrylic IOLs were evaluated by AFM. Analysis was performed at room temperature (21 degrees C) in a liquid environment using the force-versus-distance mode of a commercial instrument (NanoScope III). Measurements were acquired with rectangular silicon cantilevers of a nominal elastic constant of 10 Newton/m. The nominal value of the tip's radius of curvature was 1 mum, and the scanning speed during the acquisitions ranged from 10 to 400 nm/s. The adhesion force measurements showed different characteristics for the various types of IOLs (P<.001, analysis of variance). The hydrophobic acrylic IOL had the largest mean adhesive force (283.75 nanoNewton [nN] +/- 0.14 [SD]) followed by the hydrophilic acrylic (84.76 +/- 0.94 nN), PMMA (45.77 +/- 0.47 nN), and silicone (2.10 +/- 0.01 nN) IOLs. The surface properties of the biomaterials used to manufacture IOLs are important because they can influence the incidence and severity of posterior capsule opacification (PCO). Although further studies are necessary to elucidate the mechanism of PCO development and the interface interactions between the IOL and capsule, the results in this study may bolster the theory of manufacturing more-adhesive materials to prevent PCO.

New nanostructured hybrid membranes for gas separation have been prepared and characterized for the first time in the literature by using a block copolymer, poly(styrene-b-butadiene-b-styrene) (SBS), and aminated SBA-15. Short mesopore channels, platelet SBA-15 particles with a high surface density of 3-aminopropyl grafts (3.8 nm⁻²) and modest surface area reduction (45%) were prepared, characterized and used as a filler. The gas transport characterization of the hybrid membranes indicates that with a 10 wt% content of aminated filler, outstanding performances in terms of selectivity and permeability for the CH₄/N₂ and the CO₂/N₂ gas pairs can be obtained. In particular, the CH₄/N₂ ideal selectivity of 7.3 is higher than the values of the existing block co-polymers used for this separation and of mixed matrix membranes described to date in the literature. Membranes with such a high separation factor may enable the exploitation of natural gas with high N₂ content and increase the amount of methane that can be economically recovered. The combination of the CO₂/N₂ ideal selectivity of 53 with a CO₂ permeability of 173 Barrer demonstrates that the new hybrid membranes prepared in this study deserve further attention as a practical commercial solution also for the post-combustion capture of carbon dioxide. Finally, the small and flat particles dispersed in the polymer lend themselves to the fabrication of thin industrial membranes with enhanced productivity.

We report on our latest studies on alignment of chromonic liquid crystals, a special class of molecules which recently attracted the attention of researchers. In particular, we show a detailed study of planar anchoring of disodium cromoglycate (DSCG) and, for the first time in the literature, a stable homeotropic alignment, achieved using a surface property of the alignment layer, i.e. the hydrophobicity. Excellent candidates from this point of view are pure polybutadiene (PB) and polydimethylsiloxane (PDMS). In fact, for the former the homeotropic anchoring stabilizes after one day, while for the latter stabilization occurs soon after cooling from the isotropic phase. After a long time both types of alignments (planar and homeotropic) evolve into thermodynamically stable configurations, i.e. ribbon structures. An explanation of the behaviour is given.

Purpose.: To investigate the depth-dependent mechanical anisotropy of the human corneal stroma at the tissue (stroma) and molecular (collagen) level by using atomic force microscopy (AFM). Methods.: Eleven human donor corneas were dissected at different stromal depths by using a microkeratome. Mechanical measurements were performed in 15% dextran on the surface of the exposed stroma of each sample by using a custom-built AFM in force spectroscopy mode using both microspherical (38-μm diameter) and nanoconical (10-nm radius of curvature) indenters at 2-μm/s and 15-μm/s indentation rates. Young's modulus was determined by fitting force curve data using the Hertz and Hertz-Sneddon models for a spherical and a conical indenter, respectively. The depth-dependent anisotropy of stromal elasticity was correlated with images of the corneal stroma acquired by two-photon microscopy. Results.: The force curves were obtained at stromal depths ranging from 59 to 218 μm. At the tissue level, Young's modulus (E_S) showed a steep decrease at approximately 140-μm stromal depth (from 0.8 MPa to 0.3 MPa; P = 0.03) and then was stable in the posterior stroma. At the molecular level, Young's modulus (E_C) was significantly greater than at the tissue level; E_C decreased nonlinearly with increasing stromal depth from 3.9 to 2.6 MPa (P = 0.04). The variation of microstructure through the thickness correlated highly with a nonconstant profile of the mechanical properties in the stroma. Conclusions.: The corneal stroma exhibits unique anisotropic elastic behavior at the tissue and molecular levels. This knowledge may benefit modeling of corneal behavior and help in the development of biomimetic materials.