We report nonreciprocal dissipation-less transport in single ballistic InSb nanoflag Josephson junctions. Applying an in-plane magnetic field, we observe an inequality in supercurrent for the two opposite current propagation directions. Thus, these devices can work as Josephson diodes, with dissipation-less current flowing in only one direction. For small fields, the supercurrent asymmetry increases linearly with external field, and then it saturates as the Zeeman energy becomes relevant, before it finally decreases to zero at higher fields. The effect is maximum when the in-plane field is perpendicular to the current vector, which identifies Rashba spin-orbit coupling as the main symmetry-breaking mechanism. While a variation in carrier concentration in these high-quality InSb nanoflags does not significantly influence the supercurrent asymmetry, it is instead strongly suppressed by an increase in temperature. Our experimental findings are consistent with a model for ballistic short junctions and show that the diode effect is intrinsic to this material.

The behavior of liquid Au–Si alloys on Si surfaces covered by a monolayer of gold has been investigated by ultrahigh-vacuum scanning electron microscopy. On the (111) surface, the alloy displays a constant contact angle with the surface from the eutectic temperature up to a temperature of 650 °C and thereafter the contact angle increases linearly with temperature. As observed in previous work, the shape of the liquid droplets changes from circular at lower temperature to hexagonal at higher temperature. In contrast, on the (100) surface, the contact angle increases linearly from the eutectic temperature to high temperature. The behavior of the shape of the droplets is, however, reversed: it is polygonal (octagonal) at lower temperature and becomes round at higher temperature. This behavior is explained in terms of the relative surface energy of the two surfaces and changing line tension of the liquid–solid–vapor phase line. In addition, the behavior of Au–Si droplets on vicinal and patterned surfaces of Si has been examined. The droplets cause step bunching and modify the local surface structure. Solidification of the droplets on all surfaces leads to phase separation.