This paper presents the formulation, characterization, and in vitro studies of polymer composite material impregnated with naturally derived hydroxyapatite (HA) particulates for biomedical implant applications. Laevistrombus canarium (LC) seashells (SS) were collected, washed and cleaned, sun-dried for 24 h, and ground into powder particulates. The SS particulates of different weight percentages (0, 10, 20, 30, 40, 50 wt%)-loaded high-density polyethylene (HDPE) composites were fabricated by compression molding for comparative in vitro assessment. A temperature-controlled compression molding technique was used with the operating pressure of 2 to 3 bars for particulate retention in the HDPE matrix during molding. The HDPE/LC composite was fabricated and characterized using X-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM), energy-dispersive X-ray (EDX), differential scanning calorimetry (DSC), and TGA. Mechanical properties such as tensile, compression, flexural, hardness, and also surface roughness were tested as per ASTM standards. Mass degradation and thermal stability of the HDPE/LC composite were evaluated at different temperatures ranging from 10 to 700 °C using thermogravimetric analysis (TGA). The maximum tensile strength was found to be 27 ± 0.5 MPa for 30 wt% HDPE/LC composite. The thermal energy absorbed during endothermic processes was recorded as 71.24 J/g and the peak melting temperature (Tm) was found to be 128.4 °C for the same 30 wt% of HDPE/LC composite specimen. Excellent cell viability was observed during the in vitro biocompatibility study for EtO-sterilized 30 wt% of HDPE/LC composite specimen, except for a report of mild cytotoxicity in the case of higher concentration (50 µL) of the MG-63 cell line. The results demonstrate the potential of the fabricated composite as a suitable biomaterial for medical implant applications.

Polyether Ether Ketone (PEEK) exhibits superior mechanical and biological safety characteristics, and its biological inertness significantly restricts its applicability in biomedical applications. Recent researches included active ceramic particles to enhance biological activity and broaden the application range of bioactive composites in medical implants. During the current investigation, acrylic acid-functionalized ceramic TiO₂ and SiO₂ nanoparticles (NP) were used to reinforce the PEEK matrix. The PEEK/TiO₂/SiO₂ (PTS) nanocomposite was fabricated using plastic injection moulding process. Different functional groups and crystal plane orientations of the composite were found through FTIR and XRD. The morphological and elemental analysis were carried out using FESEM and the EDAX mapping technique. The thermal stability of the composite was investigated through TGA and DSC analysis. The mean diameter of the inhibition zone of PTS polymer composite is 18.125 mm and 16.375 mm against E. coli and B. subtilis, respectively, which is higher than that of the mean diameter of the inhibition zone of PEEK. In-vitro direct and indirect cytotoxicity studies were carried using the MG-63 cell line and found the cell viability as 94.30% and cytotoxicity as 5.70% on PTS nanocomposite. Cell adhesion study was carried out using MG-63 cell line on the composite surface. That demonstrated the good cell adherence and cell proliferation those were observed through SEM morphologies. Thus, the newly developed composite serves as a potential candidate in biomedical applications.

The growing field of dental implant research and development has emerged to rectify the problems associated with human dental health issues. Bio-ceramics are widely used in the medical field, particularly in dental implants, ortho implants, and medical and surgical tools. Various materials have been used in those applications to overcome the limitations and problems associated with their performance and its impact on dental implants. In this article we review and describe the fabrication methods employed for ceramic composites, the microstructure analyses used to identify significant effects on fracture behaviour, and various methods of enhancing mechanical properties. Further, the collective data show that the sintering technique improves the density, hardness, fracture toughness, and flexural strength of alumina- and zirconia-based composites compared with other methods. Future research aspects and suggestions are discussed systematically.

This research aims to develop a nontoxic PEEK-based acrylic acid-functionalized nTiO₂ reinforced polymer nanocomposite fabricated by injection molding. Functional groups in PEEK, synthesized nTiO₂, and PEEK+nTiO₂ composite have been identified through FTIR analysis. Effect of acrylic acid-functionalized nTiO₂ particles on the thermal degradation was investigated using DSC, TGA analysis, and biocompatibility of PEEK+nTiO₂ using in-vitro studies. The cytotoxicity level as 2.7% (grade 1, slight toxic level) and cell viability as 97.3% were identified in the direct method of cytotoxicity assessment. The indirect cytotoxicity method revealed slight toxic level. Excellent cell growth was identified through cell adhesion study using SEM analysis. Graphical abstract