The recent rapid development in perovskite solar cells (PSCs) has led to significant research interest due to their notable photovoltaic performance, currently exceeding 25% power conversion efficiency for small-area PSCs. The materials used to fabricate PSCs dominate the current photovoltaic market, especially with the rapid increase in efficiency and performance. The present work reviews recent developments in PSCs’ preparation and fabrication methods, the associated advantages and disadvantages, and methods for improving the efficiency of large-area perovskite films for commercial application. The work is structured in three parts. First is a brief overview of large-area PSCs, followed by a discussion of the preparation methods and methods to improve PSC efficiency, quality, and stability. Envisioned future perspectives on the synthesis and commercialization of large-area PSCs are discussed last. Most of the growth in commercial PSC applications is likely to be in building integrated photovoltaics and electric vehicle battery charging solutions. This review concludes that blade coating, slot-die coating, and ink-jet printing carry the highest potential for the scalable manufacture of large-area PSCs with moderate-to-high PCEs. More research and development are key to improving PSC stability and, in the long-term, closing the chasm in lifespan between PSCs and conventional photovoltaic cells.

B, N-codoped titania mesoporous crystals were prepared by the sol–gel method followed by a molten nitrate process to modify the sample morphology. The composition, morphology and microstructure of the obtained samples were characterized by X-ray diffraction (XRD), X-ray photoemission spectroscope (XPS), Brunauer Emmett Teller (BET), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and selected area electron diffraction (SAED). Fourier Transform Infrared spectroscopy (FTIR) revealed weak complex vibrations between the Ti–O oxide species and the unsaturated sites (Ti³⁺) through the incorporation of hydroxyl groups, which was not observed in the bulk titania (B–N–TiO₂). The photocatalytic reactivity of boron-nitrogen codoped TiO₂ was examined for the removal of methylene blue (MB) under visible light irradiation. The nitrates treated B-doped TiO₂ exhibited better photocatalytic activity for dye degradation than that of B-doped TiO₂ and nitrates treated TiO₂. The best performance was obtained in the sample treated at a calcination temperature of 550 °C.

Lead-free, bismuth-based perovskite solar cells (PSCs) are promising, non-toxic, and stable alternatives to lead-based PSCs, which are environmentally harmful and highly unstable under deprived air conditions. However, bismuth-based PSCs still suffer from low-power-conversion efficiency (PCE) due to their large bandgap and poor film morphology. Their poor film-forming ability is the greatest obstacle to Cs₃Bi₂I₉ progress in thin-film solar cell technology. This study synthesizes novel, lead-free perovskites with a small bandgap, excellent stability, and highly improved photovoltaic performance by integrating different amounts of potassium iodide (KI) into a perovskite precursor solution. KI incorporation improves the crystallinity of the perovskite, increases the grain size, and decreases the potential contact distribution, which is demonstrated by X-ray diffraction, electronic scanning microscopy, atomic force microscopy, and ultraviolet-visible spectroscopy. The Cs₃Bi₂I₉ PSC device with 2 vol. % incorporation of KI shows the highest PCE of 2.81% and Voc of 1.01 V as far as all the Bi-based cells fabricated for this study are concerned. The study demonstrates that incorporating KI in the Cs₃Bi₂I₉ perovskite layer highly stabilizes the resultant PSC device against humidity to the extent that it maintains 98% of the initial PCE after 90 days, which is suitable for solar cell applications. The devices also demonstrate greater resistance to airborne contaminants and high temperatures without encapsulation, opening up new possibilities for lead-free Cs₃Bi₂I₉ PSCs in future commercialization.

Heavy metals such as cadmium (Cd) pollute the environment. Heavy metal pollution endangers the Nile River since it serves as an irrigation and freshwater source for the cities and farms that line its banks. Water and sediment samples from the Nile River were tested for Cd content. In addition, a sequential experiment analytical method was performed to determine the metal’s relative mobility. According to the data, there is an average of 0.16 mg kg⁻¹ of Cd in sediments. The BeniSuef water treatment plant and brick factory, the iron and steel factory of Helwan, the oil and detergent factory of Sohag, and the discharge of the cement factory in Samalut had the greatest concentration of Cd in their vicinity. According to the risk assessment code, there are four categories of Cd: residual (57.91%), acid-soluble (27.11%), reducible (11.84%), and oxidizable (3.14%). Bioavailable and mobile Cd levels in sediment and water were found in Beni Suef, Aswan; Helwan; Samalut; Sohag; and Helwan. Because the other metal is highly bioavailable, its concentration is not a risk factor at the Samalut station. Cd’s toxicity and bioaccumulation make it an extra hazard to aquatic animals and human life. There should be a deterministic approach to monitoring Cd near industrial sources.