A novel electrochemical sensor for determining trace levels of Hg²⁺, Pb²⁺, and Zn²⁺ ions in water using square wave voltammetry (SWV) is reported. The sensor is based on a platinum electrode (Pt) modified by poly(3,4-ethylenedioxythiophene) and N _α,N _α-bis-(carboxymethyl)-l-lysine hydrate (NTA lysine) PEDOT/NTA. The modified electrode surface (PEDOT/NTA) was prepared via the introduction of the lysine-NTA group to a PEDOT/N-hydroxyphthalimide NHP electrode. The (PEDOT/NTA) was characterized via cyclic voltammetry (CV), Fourier transform infrared (FTIR) spectroscopy, and scanning electron microscopy (SEM). The effects of scan rates on the electrochemical properties of the polymer electrode were also investigated. The electrochemical results were used to estimate the coverage of the electrode polymer surface and its electrostability in background electrolyte solutions. Several analytical parameters, such as polymer film thickness, metal deposition time, and pH of the electrolyte, were examined. Linear responses to Hg²⁺, Pb²⁺, and Zn²⁺ ions in the concentration range of 5-100 μg L^-1 were obtained. The limits of detection (LODs) for the determination of Hg²⁺, Pb²⁺, and Zn²⁺ ions were 1.73, 2.33, and 1.99 μg L^-1, respectively. These promising results revealed that modified PEDOT/NTA films might well represent an important addition to existing electrochemical sensor technologies.

This work will show, for the first time, the effect of nicotinic acid (NA) and 2-methylnicotinic acid (MNA)on the synthesis and properties of conducting polyaniline (PANI). The work investigates the effects of sulphuric acid (H2SO4), nicotinic acid (NA), and 2-methylnicotinic acid (MNA) on the synthesis and properties of polyaniline. The results show that the preparation of polyaniline from a sulphuric acid electrolyte is faster than the preparation from nicotinic acid and 2- methylnicotinic acid electrolytes. Moreover, the electrical conductivity and thermal stability of PANI/H2SO4 were greater than PANI/NA and PANI/MNA. All the polymers prepared in this study were identified using FT-IR. Scanning electron microscopy (SEM) was used to examine the morphologies of the PANI samples, from which it was determined that PANI/H2SO4 has a fibrous and open structure with a higher porosity morphology compared to PANI/NA and PANI/MNA. The electrical conductivities of the PANI samples were measured as 1.09 S cm-1, 0.65 S cm-1 and 0.089 S cm-1 for PANI/H2SO4, PANI/NA and PANI/MNA, respectively. The thermal stability of PANI was examined using the Thermogravimetric Analysis (TGA) technique. PANI/H2SO4 was found to degrade between 450-500°C, while PANI/NA and PANI/MNA decomposed at temperatures between 300-400°C.