Superposed perfobond connectors are a type of connector used in composite structures. When the construction conditions are limited to increase the diameter of the opening, the shear capacity of the connector can be improved by enhancing the confining effect of the concrete dowel. In this study, 12 superposed perfobond connectors were fabricated to investigate the influence of lateral constraints on their shear behavior. The effects of hole area and holes’ number, diameter of the perforating rebar, concrete compressive strength, and the number of transverse reinforcements were investigated via the failure modes and load–slip curves. The results indicate that double-sided shear failure occurs in connectors with perfobond rib thicknesses exceeding 9 mm, and the connectors featuring strong lateral constraints not only exhibited higher bearing capacities but also superior load-holding capacities after peak load. Finally, an equation for the shear capacity of multi-hole perfobond connectors, considering lateral constraints, was proposed according to the double-sided shear theory.

To enhance the standardization and construction efficiency of prefabricated steel structures and to promote the application of cold-formed steel tubes with the advantages of high standardization, superior mechanical properties, and fast processing speeds, two types of composite beam to concrete-filled cold-formed high-strength square steel tubular column joints with different connection forms were designed in this study: the external diaphragm joint (ED joint) and the through diaphragm joint (TD joint). These joints were subjected to cyclic loading tests to evaluate the influence of the connection designs on key seismic performance parameters, such as failure modes, load-bearing capacities, the degradation of strength and stiffness, ductility, and energy dissipation capabilities. The results show that both the ED and TD joints experienced butt weld fractures at the bolted-welded connections on the beam, effectively transferring the plastic hinges from the joint zone to the beam and demonstrating good seismic performance. The ED joint specimen JD1 and the TD joint specimen JD2 exhibited similar load-bearing capacity, stiffness, strength degradation, and energy dissipation capacity. However, the TD joint showed lower ductility compared to the ED joint due to premature weld fractures. A nonlinear finite element model (FEM) was developed using MSC.MARC 2012, and the numerical simulation showed that the FEM could effectively simulate the hysteresis performance of the composite beam to concrete-filled, cold-formed, high-strength, square, steel tubular column joints with external and through diaphragms.

In recent years, the researches on concrete-filled steel tubular (CFST) intersecting nodes mainly focused on the plane intersecting nodes, while that on space intersecting nodes with off-plane angles was relatively less. In this study, the nonlinear analyses of CFST space intersecting node models established in ABAQUS were performed under the monotonic axial compression and reciprocal axial tension-compression loads, respectively. The stress distributions of steel tubes and core concrete were analyzed, and the hysteresis characteristics and stiffness degradation of the node were studied. The in-plane angle, off-plane angle, out-of-plane constraint effect, steel tube diameter-to-thickness ratio, and core concrete strength were used as control parameters to analyze their effects on the mechanical behavior of the nodes. The results show that the bearing capacity of the nodes meets the design requirements, the hysteresis loop is full, the initial stiffness is large and the stiffness degrades slowly. The off-plane angle, out-of-plane constraint effect, steel tube diameter-thickness ratio and core concrete strength have significant effects on the bearing capacity and lateral stiffness of the nodes. In order to reduce the adverse effect of out-of-plane displacement, the space intersecting nodes in practical engineering can use reinforced floor beams or prestressd cables to impose out-of-plane constraint, and the recommended value of out-of-plane constraint effect is 10–30 kN/mm.

This study reveals the Vierendeel mechanism of hybrid high-strength steel composite cellular beams (HHS-CCBs) through experimental investigation and finite element analysis (FEA). The forces acting on the openings of composite cellular beams (CCBs) are further analyzed. A calculation method is developed to evaluate the load-carrying capacity of HHS-CCBs under the combined action of bending moment and shear force, which takes into account the shear contributions of the concrete slab and beam flange at circular openings. The accuracy of the proposed formula and the influence of key parameters on load-carrying capacity are thoroughly examined through FEA. The results indicate that within the range of D = 0.6h_s − 0.7h_s and L = 0.7h_s − 1.0h_s (D and L represent the hole diameter and edge distance, respectively; h_s is the height of the steel beam), stress concentration at the beam-end welds could be avoided, the formation of Vierendeel mechanism at the beam-end opening could be ensured, and excessive reduction in load-carrying capacity could be prevented. Furthermore, the high-strength steel (HSS) flange strength and location had a minimal effect on the failure mode of HHS-CCBs. As the flange strength increased, full plasticity was not achieved in the cross-section, and the load-carrying capacity increased nonlinearly. Asymmetric specimens with HSS in the lower flange only and symmetric specimens with HSS in both the upper and lower flanges exhibited comparable load-carrying capacities. The load-carrying capacity calculation formula is applicable to HHS-CCBs with different section types, provided that circular holes are present in the beam web and Vierendeel mechanism damage occurs. However, the flange width–thickness ratio must not significantly exceed the specified limit.