Microwave devulcanization is known to be a promising and an efficient rubber recycling method which makes possible for the rubber to regain its fluidity, and makes it capable of being remolded and revulcanized. The focus of this work is to understand the physical and chemical changes that occur in the ground tire rubber after different microwave exposure periods. For this purpose chemical, thermal, rheological and morphological analyses were performed on the tire rubber, which contains natural rubber (NR) and styrene-butadiene rubber (SBR) as polymeric material. The results showed that the microwave treatment promoted the breaking of sulfur cross-links and consequently increased the rubber fluidity. However, long periods of exposure led to degradation and modification of some properties. At nanoscale, the deformation of the devulcanized NR domain under stress was observed, and the morphology obtained appears to be a droplet dispersion morphology. The most exposed samples presented only one glass transition temperature, and from this it was concluded that the treatment may have played an important role in the compatibilization of the elastomeric blend. Based on the results, it is required to control the microwave exposure time and polymeric degradation in order to achieve a regenerated rubber with satisfactory properties

The recycling of waste rubber has considerable significance in terms of environmental protection and energy conservation. Considering that most of the relevant literature is concerned with tire recycling, the objective of this study is to develop and characterize styrene-butadiene rubber composites containing only industrial rubber scraps devulcanized by microwave. The styrene-butadiene rubber extruded profile scraps were collected and ground under ambient conditions. The obtained powder styrene-butadiene rubber-r was physically, thermally, and chemically characterized. From the devulcanized styrene-butadiene rubber-r two composites were prepared, varying the exposure time of the powder in the microwave (3 and 4 min). These composites were compared to a control sample supplied by the industry from which the styrene-butadiene rubber extruded profile scraps were collected. Vulcanization parameters were determined by oscillatory disk rheometry. Vulcanized composites were characterized by crosslink density and physical-mechanical properties (Shore A hardness, tensile and tear strength, and compression set) before and after a postcure process. The mechanical properties of the compositions were ∼25% for tensile strength and 41% for tear strength compared to the control sample. The results for the crosslink density verified those for the mechanical properties of the composites.