A novel three-dimensional graphene-like networks material (3D-GLN) exhibiting the hierarchical porous structure was fabricated with a large-scale preparation method by employing an ion exchange resin as a carbon precursor. 3D-GLN was first studied as the effective microwave absorbing material. As indicated from the results of the electromagnetic parameter tests, and the minimum reflection loss (R_L) of the 3D-GLN reached −34.75 dB at the frequency of 11.7 GHz. To enhance the absorption performance of the nonmagnetic 3D-GLN, the magnetic Fe₃O₄ nanoparticles were loaded on the surface of the 3D-GLN by using the hydrothermal method to develop the 3D-GLN/Fe₃O₄ hybrid. The hybrid exhibited the prominent absorbing properties. Under the matching thickness of 3.0 mm, the minimum R_L value of hybrid reached −46.8 dB at 11.8 GHz. In addition, under the thickness range of 2.0–5.5 mm, the effective absorption bandwidth (R_L < 10 dB) was 13.0 GHz, which covered part of the C-band and the entire X-band, as well as the entire Ku-band. The significant microwave absorption could be attributed to the special 3D network structure exhibited by the hybrid and the synergistic effect exerted by the graphene and the Fe₃O₄ nanoparticles. As revealed from the results, the 3D-GLN/Fe₃O₄ hybrid could be a novel microwave absorber with promising applications.

Although the content of Eu in the single crystal (La_0.8Eu_0.2)_4/3Sr_5/3Mn₂O₇ is very small, the effects of Eu ions on the magnetic and transport properties are quite evident at low temperature due to the large size difference between Eu and La ions, compared with the crystal’s parent compound La_5/3Sr_4/3Mn₂O₇. The sharp jumps in M( H) and ρ ( H) curves suggest that a first-order Field-induced transition from magnetically disorder state to 3D long-range ferromagnetic metallic state takes place at 2 K. Both resistivity and magnetization dependents on the magnetic history and clearly demonstrate hysteretic behaviors. These results indicate that the system has a very fragile ground state and the local lattice distortions in bilayer manganites play an important role in the physical properties.

The arc-melting method was adopted to prepare the compound La_0.5Pr_0.5(Fe_1−xCo_x)_11.4Si_1.6 (x = 0, 0.02, 0.04, 0.06, 0.08), and the magnetocaloric effect of the compound was investigated. As indicated by the powder X-ray diffraction (XRD) results, after receiving 7-day high temperature annealing at 1373 K, all the compounds formed a single-phase cubic NaZn₁₃ crystal structure. As indicated by the magnetic measurement, the most significant magnetic entropy change |∆S_M(T)| of the sample decreased from 28.92 J/kg·K to 4.22 J/kg·K with the increase of the Co content under the 0–1.5 T magnetic field, while the Curie temperature T_C increased from 185 K to the room temperature 296 K, which indicated that this series of alloys are the room temperature magnetic refrigerant material with practical value. By using the ferromagnetic Curie temperature theory and analyzing the effect of Co doping on the exchange integral of these alloys, the mechanism that the Curie temperature of La_0.5Pr_0.5(Fe_1−xCo_x)_11.4Si_1.6 and La_0.8Ce_0.2(Fe_1−xCo_x)_11.4Si_1.6 increased with the increase in the Co content was reasonably explained. Accordingly, this paper can provide a theoretical reference for subsequent studies.