Bone tissue engineering has been developed in the past decades, with the engineering of bone substitutes on the vanguard of this regenerative approach. Polycaprolactone-based scaffolds are fairly applied for bone regeneration, and several composites have been incorporated so as to improve the scaffolds’ mechanical properties and tissue in-growth. In this study, hydroxyapatite is incorporated on polycaprolactone-based scaffolds at two different proportions, 80:20 and 60:40. Scaffolds are produced with two different blending methods, solvent casting and melt blending. The prepared composites are 3D printed through an extrusion-based technique and further investigated with regard to their chemical, thermal, morphological, and mechanical characteristics. In vitro cytocompatibility and osteogenic differentiation was also assessed with human dental pulp stem/stromal cells. The results show the melt-blending-derived scaffolds to present more promising mechanical properties, along with the incorporation of hydroxyapatite. The latter is also related to an increase in osteogenic activity and promotion. Overall, this study suggests polycaprolactone/hydroxyapatite scaffolds to be promising candidates for bone tissue engineering, particularly when produced by the MB method.

Biomaterial properties and controlled architecture of scaffolds are essential features to provide an adequate biological and mechanical support for tissue regeneration, mimicking the ingrowth tissues. In this study, a bioextrusion system was used to produce 3D biodegradable scaffolds with controlled architecture, comprising three types of constructs: (i) poly(ε-caprolactone) (PCL) matrix as reference; (ii) PCL-based matrix reinforced with cellulose nanofibers (CNF); and (iii) PCL-based matrix reinforced with CNF and hydroxyapatite nanoparticles (HANP). The effect of the addition and/or combination of CNF and HANP into the polymeric matrix of PCL was investigated, with the effects of the biomaterial composition on the constructs (morphological, thermal, and mechanical performances) being analysed. Scaffolds were produced using a single lay-down pattern of 0/90°, with the same processing parameters among all constructs being assured. The performed morphological analyses showed a satisfactory distribution of CNF within the polymer matrix and high reliability was obtained among the produced scaffolds. Significant effects on surface wettability and thermal properties were observed, among scaffolds. Regarding the mechanical properties, higher scaffold stiffness in the reinforced scaffolds was obtained. Results from the cytotoxicity assay suggest that all the composite scaffolds presented good biocompatibility. The results of this first study on cellulose and hydroxyapatite reinforced constructs with controlled architecture clearly demonstrate the potential of these 3D composite constructs for cell cultivation with enhanced mechanical properties.

Bone tissue regeneration remains a significant challenge in clinical settings due to the complexity of replicating the mechanical and biological properties of bone environment. This study addresses this challenge by proposing a hybrid scaffold designed to enhance both bioactivity and physical stability for bone tissue regeneration. This research is the fisrt to develop a rigid 3D structure composed of polycaprolactone (PCL) and hydroxyapatite nanoparticles (nHA) integrated with a bioink containing human dental pulp stem/stromal cells (hDPSCs), alginate, nHA and collagen (Col). The biofabricated constructs were extensively characterized through cytocompatibility tests, osteogenic differentiation assessment, and biocompatibility evaluation in a rat model. In vitro results demontrated that the hybrid scaffolds presented significantly higher cell viability after 168 h compared to the control group. Furthermore, the hybrid scaffolds showed increased osteogenic differentiation relative to other groups. In vivo evaluation indicated good biocompatibility, characterized by minimal inflammatory response and successful tissue integration. These findings highlight the scaffold's potential to support bone tissue regeneration by combining the mechanical strength of PCL and nHA with the biological activity of the alginate-nHA-Col and hDPSCs bioink. The current study provides a promising foundation for the development of biomaterials aimed at improving clinical outcomes in bone repair and regeneration, particulary for the treatment of critical-size bone defects, targeted drug administration, and three-dimensional models for bone tissue engineering.

Notwithstanding the advances achieved in the last decades in the field of synthetic bone substitutes, the development of biodegradable 3D-printed scaffolds with ideal mechanical and biological properties remains an unattained challenge. In the present work, a new approach to produce synthetic bone grafts that mimic complex bone structure is explored. For the first time, three scaffolds of various composition, namely polycaprolactone (PCL), PCL/hydroxyapatite nanoparticles (HANp) and PCL/HANp/diacrylate poly(ethylene glycol) (PEGDA), were manufactured by extrusion. Following the production and characterisation of the scaffolds, an in vitro evaluation was carried out using human dental pulp stem/stromal cells (hDPSCs). Through the findings, it was possible to conclude that, in all groups, the scaffolds were successfully produced presenting networks of interconnected channels, adequate porosity for migration and proliferation of osteoblasts (approximately 50%). Furthermore, according to the in vitro analysis, all groups were considered non-cytotoxic in contact with the cells. Nevertheless, the group with PEGDA revealed hydrophilic properties (15.15° ± 4.06) and adequate mechanical performance (10.41 MPa ± 0.934) and demonstrated significantly higher cell viability than the other groups analysed. The scaffolds with PEGDA suggested an increase in cell adhesion and proliferation, thus are more appropriate for bone regeneration. To conclude, findings in this study demonstrated that PCL, HANp and PEGDA scaffolds may have promising effects on bone regeneration and might open new insights for 3D tissue substitutes.

Bone tissue engineering has been developed in the past decades, with the engineering of bone substitutes on the vanguard of this regenerative approach. PCL based scaffolds are fairly applied for bone regeneration, and several composites have been incorporated, as to improve the devices’ mechanical properties and tissue ingrowth. In this study, HA was incorporated on PCL based scaffolds with two different proportions, 80:20 and 60:40. Devices were produced with two different techniques, SC and MB, and further investigated with regards to their mechanical characteristics and in vitro cytocompatibility. Results show the MB devices to present more promising mechanical properties, along with the incorporation of HA. The latter is also related to an increase in osteogenic activity and promotion. Overall, this study suggest PCL:HA scaffolds to be promising candidates for bone tissue engineering, particularly when produced by the MB method.