In this paper, we report the application of zinc phosphate electrostatic-painting top coating on cold sprayed AA7075 leading to a significant improvement in corrosion-fatigue performance. High strength AA7075 powder was sprayed on AZ31B substrate, followed by the application of the top coating. The electrochemical corrosion and corrosion-fatigue tests of the coated and uncoated specimens were performed in 3.5% NaCl solution. Transmission electron microscopy (TEM) analysis showed that a continuous nanolayered mixture of Mg/Al was formed at the cold spray coating/substrate interface leading to high bonding strength. The results showed that the combined coatings improved the corrosion resistance remarkably, and significantly increased the fatigue life, with a fatigue strength of 80 MPa at 10⁷ cycles, as compared to the as-cast specimen. Surface topographic analysis of the corrosion-fatigue-tested specimens demonstrated the presence of deep macro-pits on the cold sprayed AA7075 coating after 3.7 million cycles, while there were no such pits on the top-coated specimens, even after 10⁷ cycles when tested at 30 Hz. The fractographic analysis of the fatigue-fractured specimens showed that the formation of pits allowed the NaCl solution to penetrate in the AZ31B substrate, creating localized corrosion pits resulting in premature failure, which eventually reduced the fatigue life.

The influences of the forging process and micro-arc oxidation (MAO) coating on the corrosion behavior of ZK60 wrought magnesium alloys exposed to salt spray and constant stress corrosion conditions were investigated. The microstructure of the ZK60 Mg alloy specimens forged under different temperatures (i.e., 250, 300, and 450 °C) was characterized using metallography, EBSD, and SEM. It was demonstrated that the ZK60 alloy forged at 300 °C (i.e., ZK60EF-300) had finer grain and uniformly distributed β-phase and, thus, better corrosion resistance than the ZK60 forged at 450 °C. At the lower forging temperature (250 °C) twins formed in the ZK60 alloy, which accelerated the corrosion of the ZK60E-250 specimen. The MAO coating provided robust corrosion protection for all the ZK60 wrought Mg alloy substrates. The salt spray corrosion test results showed that when the MAO coating broke down at certain weak sites, the corrosion performance of the coated Mg alloy was predominantly determined by the alloy substrate. The stress corrosion behaviors of the uncoated and MAO-coated ZK60 alloy specimens were also investigated under a constant load of 80 MPa in 3.5 wt.% NaCl solution. The MAO coating was found to improve the stress-corrosion resistance of the ZK60 alloy pronouncedly.