The effect of contamination of polypropylene (PP) with selected polymers is studied to simulate the effect of mis-sorting in recycling streams. Polystyrene (PS), polyethylene terephthalate (PET), polycarbonate (PC), acrylonitrile butadiene styrene (ABS), and polylactic acid (PLA) were compounded with PP at different concentrations varying between 3 and 10%. Infrared spectroscopy proved the absence of chemical bonds between the constituents. Generally, melt flowability, except for the PP/PLA blend, and crystallinity were only slightly affected by the incorporation of the contaminating polymers. Samples of the polymer blends were injection moulded and further tested for their tensile and impact properties. Critical behaviour was induced by the introduction of a weld line as a result of the application of multiple gating points during injection moulding. Results generally show the applicability of PP mixtures within the investigated range of contamination, without much sacrifice in mechanical performance. However, in the case of ABS and PLA, more care should be taken when designing complex parts with weld lines, due to reduced toughness.

In this study, the behavior of greases during oscillating bearing operation with a small oscillation angle and high frequency was investigated. This mode of operation entails demands on the lubrication system that differ significantly from those for continuously rotating bearings. In order to determine the variables influencing the suitability of a lubricating grease for small angle oscillating operation, the grease samples were examined with particular regard to their rheological properties. The focus of this investigation was to find a relationship between the rheological parameters and the real behavior in the bearing. Therefore, rheological and physical parameters, which influence the long-term structural changes and lubrication conditions, were identified. For this purpose, the viscosity was measured over a wide shear-rate range. The storage and loss modulus, the work of deformation, and the adhesion force jump are also determined. Afterward, rotational transient flow measurements were performed. These allowed us to analyze the development of the shear stress over time, at a constant shear rate, and to examine the internal friction behavior by evaluating the energy density. Subsequently, grease-lubricated four-point bearings were used in component tests, while the frictional torque was measured. These bearings operated in oscillating motion. Moreover, the yield point of mechanically aged greases was measured and compared with that of fresh greases to examine the influence of the oscillating operation on the lubricant condition. Finally, correlations between grease composition, rheological measurements, and component tests were investigated. Thereby, parameters influencing the frictional behavior of greases in rolling bearings during oscillating operation at small swivel angles were identified.

The target of this study is to develop routes for processing Al–SiCp (SiC particulate) sheets with improved microstructures; namely, the uniform distribution of SiCp and minimized porosity throughout the whole material, thereby improving its mechanical properties. Al–SiCp composites reinforced with 5, 10, and 15 vol.% SiC and having three average sizes of 29, 17, and 8.5 µm were produced using a semi-automated stir-casting machine; finally, the bars were hot rolled to get the final sheet dimensions. The rolling steps were performed based on the results of thermomechanical simulations performed on the cast blocks. The first rolling steps were applied according to a safe rolling schedule to avoid cracking via encouraging dynamic recrystallization. The last rolling steps were performed to improve the hardness and strength of the metal matrix composites (MMCs). A refinement in grain size from an average of 420 µm in the as-cast condition to an average of about 85 µm after rolling was observed. Some heterogeneity in grain size was observed where the regions with larger, elongated grains were associated with the zones depleted by SiCp reinforcement. Reinforcing with SiCp led to a small increase in tensile strength of 10–20 MPa, and this was further improved to about 60 MPa and 110 MPa for the 5 and 10 vol.% SiCp conditions, respectively, after a T6 heat treatment.