This research focuses on investigating how physical and mechanical properties of polypropylene (PP) recycled material are modified when ultrasonic micro injection molding (UMIM) technology is used to produce material specimens. Experimental characterization by differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), Fourier transform infrared (FTIR) spectra, and rheology tests show that the fabricated PP samples were able to withstand up to five times recycled processing before some signs of mechanical and physical properties degradation are observed. Surprisingly, uniaxial extension tests show an increase of 3.07%, 10.97% and 27.33% for Young’s modulus, yield stress and ultimate stress values, respectively, and a slight reduction of 1.29% for the samples elongation at break when compared to the experimental data collected from virgin material samples. The improvement of these mechanical properties in the recycled samples suggests that ultrasonic microinjection produces a mechano-chemical material change.

Using experimental measurements and numerical computations, this paper focuses on studying the evolution of the plastic zone and how the residual stresses change in a notched T-6061 aluminum sample. Before the crack initiation, digital image measurements were taken to visualize the evolution of the plastic zone. After the sample was fractured, the material microstructure and the residual stresses around the cracked zone were characterized through optical microscopy and X-ray diffractometry. This article describes in detail how the plastic zone evolved around the notch before the crack initiation and shows the close agreement between experimental and numerical data during the load increment. The surface residual stress values around the tip of the notched sample were also measured and computed to give a better understanding of the affected region during the fracture process.