In order to remove toxic graphene oxide (GO) from aqueous solution, attapulgite (ATP) was used as adsorbent to recycle it by adsorption. In this paper, the effects of different pH, adsorbent mass, GO concentration, time and temperature on the adsorption of GO by attapulgite were studied, and the adsorption performance and mechanism were further explored by XRD, AFM, XPS, FTIR, TEM and SEM tests. The results show that when T = 303 K, pH = 3, and the GO concentration is 100 mg/L in 50 mL of aqueous solution, the removal rate of GO by 40 mg of attapulgite reaches 92.83%, and the partition coefficient K_d reaches 16.31. The adsorption kinetics results showed that the adsorption equilibrium was reached at 2160 min, and the adsorption process could be described by the pseudo-second-order adsorption equation, indicating that the adsorption process was accompanied by chemical adsorption and physical adsorption. The isotherm and thermodynamic parameters show that the adsorption of GO by attapulgite is more consistent with the Langmuir isotherm model, and the reaction is a spontaneous endothermic process. The analysis shows that attapulgite is a good material for removing GO, which can provide a reference for the removal of GO in an aqueous environment.

Magnetic carbon-supported metal nickel has been successfully synthesized by solvothermal method and heat treatment for highly effective adsorption of various reactive dyes. Structure characterization and composition analysis demonstrated that the metal nickel nanoparticles with the size of 1–2 nm were embedded into the pore of carbon spheres. It is helpful to prevent the agglomeration and falling off of metal nickel nanoparticles on the surface of carbon spheres. The adsorption performance of the carbon-supported metal nickel nanospheres for reactive brilliant yellow R-4GLN was studied by changing the pH value and initial concentration of the solution, adsorption time, adsorption temperature, and the amount of adsorbent. The carbon-supported metal nickel showed fast and efficient adsorption activity. After 5 min of adsorption, the removal efficiency of 10 mL 25 mg·mL⁻¹ reactive brilliant yellow R-4GLN was close to 100%. The carbon-supported metal nickel composite was reused 20 times, and the removal efficiency of dye remained above 98%. It also showed good adsorption performance on various reactive dyes with wide universality, which has a certain adsorption effect on most dyes with a high utilization value in wastewater treatment.