Development of hydrophobically modified ethoxylated urethane (HEUR) rheology modifiers enabled the widespread application of waterborne paints and coatings, replacing their environmentally burdening solvent-based predecessors. However, the diisocyanates, required for the conventional synthesis of HEURs, pose severe eco-sustainability threats. In this paper, we demonstrate an innovative approach to avoiding toxic components in the preparation of rheology modifiers by obtaining a new class of water-soluble isocyanate-free hydrophobically modified ethoxylated poly(hydroxy-urethane)s (IFHEURs). The first step in the synthetic pathway was the preparation of CO₂-based five-membered poly(ethylene glycol) bis(cyclic carbonate) and its subsequent aminolysis using 4,7,10-trioxa-1,13-tridecanediamine, yielding poly(hydroxy-urethane) (PHU) prepolymers terminated with cyclic carbonate groups. The PHU prepolymers were further extended in a reactive extrusion (REX) synthesis using biobased hydrophobic diamine PRIAMINE 1075. The REX technique made it possible to overcome the typical limitations of the aminolysis reaction and to reach the desired conversion within a moderate reaction time. IFHEURs have been structurally elucidated using FT-IR and NMR spectroscopy techniques, MALDI-ToF mass spectrometry, and SEC analysis and applied as rheology modifiers. The study of their associative behavior in aqueous solutions confirmed that the architectural flexibility of the obtained IFHEURs, containing terminal and pendant hydrophobic groups, opens a perspective for tuneable thickening performance.

This study reveals insights into the transurethanization reactions leading to the aliphatic–aromatic non-isocyanate poly(carbonate-urethane)s (NIPCUs) and their structure–property relationships. The crucial impact of the alkyl chain length in 4,4′-diphenylmethylene bis(hydroxyalkyl carbamate) (BHAC) on the process of transurethanization reactions was proved. The strong susceptibility of hydroxyethyl- and hydroxybutyl carbamate moieties to the back-biting side reactions was observed due to the formation of thermodynamically stable cyclic products and urea bonds in the BHACs and NIPCUs. When longer alkyl chains (hydroxypentyl-, hydroxyhexyl-, or hydroxydecyl carbamate) were introduced into the BHAC structure, it was not prone to the back-biting side reaction. Both ¹H and ¹³C NMR, as well as FT-IR spectroscopies, confirmed the presence of carbonate and urethane (and urea for some of the samples) bonds in the NIPCUs, as well as proved the lack of allophanate and ether groups. The increase in the alkyl chain length (from 5 to 10 carbon atoms) between urethane groups in the NIPCU hard segments resulted in the increase in the elongation at break and crystalline phase content, as well as the decrease in the T_g, tensile strength, and hardness. Moreover, the obtained NIPCUs exhibited exceptional mechanical properties (e.g., tensile strength of 40 MPa and elongation at break of 130%).

In the last few years, a very wide range of oligocarbonate diols, oligomers of carbonic acid esters terminated on both sides with hydroxyl groups, have appeared on the chemical market. They are mainly used for the production of flexible segments in precious grades of polyurethanes used in biomedical engineering. Poly(carbonate-urethane) due to high resistance to oxidizing and hydrolytic agents is also an attractive material for the production of adhesives and coatings with increased resistance to weather conditions. This paper presents the current state of knowledge on the methods of synthesis and main producers of oligomerols with carbonate groups, methods of poly(carbonate-urethane) synthesis and examples of its commercial applications.