Petroleum-based plastics, such as PP, PE, PVC, etc., have become an important source of environmental pollution due to their hard degradation, posing a serious threat to the human health. Isolating nanocellulose from abundant biomass waste resources and further integrating the nanocellulose into hydrophobic transparent film (i.e., nanopaper), to replace the traditional nondegradable plastic film, is of great significance for solving the problem of environmental pollution and achieving sustainable development of society. This study respectively extracted nanocellulose from the branches of Amorpha fruticosa Linn., wheat straw, and poplar residues via combined mechanical treatments of grinding and high-pressure homogenization. Among them, the nanocellulose derived from the Amorpha fruticosa has a finer structure, with diameter of about 10 nm and an aspect ratio of more than 500. With the nanocellulose as building block, we constructed hydrophilic nanopaper with high light transmittance (up to 90%) and high mechanical strength (tensile strength up to 110 MPa). After further hybridization by incorporating nano-silica into the nanopaper, followed by hydrophobic treatment, we built hydrophobic nanopaper with transmittance over 82% and a water contact angle of about 102° that could potentially replace transparent plastic film and has wide applications in food packaging, agricultural film, electronic device, and other fields.

Wood is susceptible to swelling deformation and decay fungi due to moisture adsorption that originates from the dynamic nanopores of the cell wall and the abundant hydroxyl groups in wood components. This study employed as a modifier maleic anhydride (MAn), with the help of acetone as solvent, to diffuse into the wood cell wall, bulk nanopores, and further chemically bond to the hydroxyl groups of wood components, reducing the numbers of free hydroxyl groups and weakening the diffusion of water molecules into the wood cell wall. The derived MAn-bulked wood, compared to the control wood, presented a reduction in water absorptivity (RWA) of ~23% as well as an anti-swelling efficiency (ASE) of ~39% after immersion in water for 228 h, and showed an improvement in decay resistance of 81.42% against white-rot fungus and 69.79% against brown-rot fungus, respectively. The method of combined cell wall bulking and hydroxyl group bonding could effectively improve the dimensional stability and decay resistance with lower doses of modifier, providing a new strategy for wood durability improvement.

Water-based antimicrobial agents, used in environmentally friendly applications, are widely used in wood protection industries. Furthermore, nanomaterials as antimicrobial agents, because of their biocidal component, huge specific surface area, and unique nanoscale effect, have attracted attention in the field of biodurability. We employed aqueous dispersed nano-silver with a diameter of 10 nm~20 nm to treat poplar wood and evaluated its leaching resistance and anti-mold effect on the wood surface. The results revealed that the higher the retention of the nano-silver, the stronger the protection efficiency of the wood surface against three molds (Aspergillus niger V. Tiegh, Penicillium citrinum Thom, and Trichoderma viride Pers. ex Fr); and the leachability of the nano-silver presented a slowly growing trend with the increase in the retention. When the wood surface attained a silver retention of 0.324 g·m⁻², its anti-mold efficiency against Aspergillus niger V. Tiegh, Penicillium citrinum Thom, and Trichoderma viride Pers. ex Fr reached 80, 75, and 80%, respectively, which achieved or even exceeded the required standard value of effective mold inhibition (75%). Notably, the nano-silver leaching rate at this retention attained merely 4.75 %. The nanoparticle, well distributed on a wood surface, may promote sufficient contact with fungi as well as strong interaction with wood cell wall components, which probably contributed to the effective anti-mold efficiency and the leaching resistance. This study provided positive evidence for the anti-mold effect of nano-silver on wood surface.

Wood-based panels covered by melamine-impregnated paper are widely used in floors and furniture, due to its good surface texture, hardness, wear resistance, and waterproof function. However, there are still some problems, such as formaldehyde release from the impregnated resin, non-wood touch, and complex preparation processes. Therefore, this study designed glycidyl methacrylate (GMA) and ethyleneglycol dimethacrylate (EGDMA), combined with maleic anhydride (MAN) as a reactive catalyst, to build an active monomers system. It was first impregnated into poplar veneers, and then in-situ polymerized within the veneer using a hot pressing process, which realized the gluing of the veneer onto the wood-based panel substrate, synchronously. Such treatment aims to obtain wood-based panel composites decorated by the modified veneer, with real solid wood touch feeling, satisfied surface properties, and environment friendly glue bonding. The results indicated that the optimized reaction ratio of the active monomers (GMA:EGDMA) was 2:1 (molar ratio), and the maleic anhydride addition accounted for 6 wt.% of the total monomers. Under the optimized hot pressing condition, the modified veneer closely bonded to the wood-based panel substrate without obvious interfacial gaps. The hardness, abrasion resistance, modulus of rupture, and water resistance of the composites were significantly improved. Such results indicate that the treatment realized the perfect merging of solid wood touch feeling, environment friendly feature, and excellent properties of the composite. It was highly expected to replace the traditional melamine-impregnated paper to decorate wood-based panels, and could be potentially applied as surface decorating materials in wide areas of desktop, floor, cupboard, wardrobe, and so on.