Hydrothermal synthesis of CoMoO₄@Co₃O₄ nanocomposites on an OMEP as a multidimensional electrode, and its use in a CoMoO₄@Co₃O₄/OMEP//AC supercapacitor, which delivered large power and stable cycling.

Yolk–shell Si@void@C nanocomposites are prepared via a facile method of resorcinol-formaldehyde coating and LiOH etching, without SiO₂ pre-modification on Si particles, expensive carbon sources, or environmentally-unfriendly HF solutions. Profiting from these favorable features, Si@void@C nanocomposites exhibit considerable reversible capacities (628 mA h g⁻¹ after 100 cycles) and good rate performances.

Magnesium hydroxide, as a green inorganic flame-retardancy additive, has been widely used in polymer flame retardancy. However, magnesium hydroxide is difficult to disperse with epoxy resin (EP), and its flame-retardancy performance is poor, so it is difficult to use in flame-retardant epoxy resin. In this study, an efficient magnesium hydroxide-based flame retardant (MH@PPAC) was prepared by surface modification of 2-(diphenyl phosphine) benzoic acid (PPAC) using a simple method. The effect of MH@PPAC on the flame-retardancy properties for epoxy resins was investigated, and the flame-retardancy mechanism was studied. The results show that 5 wt% MH@PPAC can increase the limiting oxygen index for EP from 24.1% to 38.9%, achieving a V-0 rating. At the same time, compared to EP, the peak heat release rate, peak smoke production rate, total smoke production rate, and peak CO generation rate for EP/5 wt% MH@PPAC composite material decreased by 53%, 45%, 51.85%, and 53.13% respectively. The cooperative effect for PPAC and MH promotes the formation of a continuous and dense char layer during the combustion process for the EP-blend material, significantly reducing the exchange for heat and combustible gases, and effectively hindering the combustion process. Additionally, the surface modification of PPAC enhances the dispersion of MH in the EP matrix, endowing EP with superior mechanical properties that meet practical application requirements, thereby expanding the application scope for flame-retardant EP-blend materials.