The wood panel industry is constantly growing, being necessary the innovation in technologies and raw materials to improve the quality of the final product. Considering the shortage and pressure to decrease the dependence of wood, there is an interest in other renewable materials such as agricultural wastes. Among these wastes, coffee parchment is one which deserves notoriety. An alternative use for coffee parchment could be for production of particleboard in association with wood particles. This study aimed to evaluate the feasibility of using coffee parchment for production of particleboard. The following percentages of wastes were used: 0, 10, 20, 30, 40 and 50% in association to eucalyptus wood. The panels were produced with 8% of urea formaldehyde (based on dry weight of particles). The pressing cycle consisted by: pre-pressing of 0.5 MPa for 10 minutes followed by pressing of 4.0 MPa, and temperature of 160° C for 15 minutes. The compaction ratio of particleboards produced using higher quantities of parchment improved the physical properties. The properties of Water Absorption (2 and 24 h) and Thickness Swelling (2 h) decreased with increasing percentage of coffee parchment. The Thickness Swelling (24 h) showed not significant effect with an increase of coffee waste. The Modulus of Elasticity for coffee parchment particleboards was in the range 646.49 ± 112.65 to 402.03 ± 66.24 MPa, while the Modulus of Rupture ranged from 8.18 ± 1.39 to 4.45 ± 0.75 MPa. The results showed that 10% of coffee parchment could be added for production of particleboards.

Agricultural residues are materials generated in large quantities in Brazil and can accumulate to such extent as to cause environmental problems. Among agricultural residues, maize cob is one worthy of notice, and an alternative use for maize cob would be to produce particleboard panels in association with wood particles. This study aimed to evaluate the feasibility of using maize cob for production of particleboard panels. The following maize cob percentages were used: 0%, 25%, 50%, 75% and 100%, in association with particles of Pinus oocarpa wood. Panels were made with 8% of urea formaldehyde and 1% of paraffin (based on dry weight of particles). For compressing the panels, a pressure of 3.92 MPa was applied at a temperature of 160º C, for 8 minutes. Increased replacement of pinewood by maize cob residue promoted significant improvements to the properties water absorption after two hours of immersion, thickness swelling after two and after twenty-four hours of immersion. Mechanical properties had a decreasing correlation with the maize cob percentage being incorporated.