The growing demand in lighter and safer structures generates the requirement of lighter joining strategies, particularly for lightweight metal alloys, composites, and also joining dissimilar materials together. Titanium alloys stand out as the conventional choice for materials for light weight structures. Adhesive bonding of titanium is an appealing route for joint design, also for the possibility of joining it with dissimilar materials. The realization of a strong joint depends not only on the joint design and type of adhesive, but also on the preparation of the adhering surface. Laser texturing presents advantages compared to common surface preparation processes in terms of eco-compatibility, energetic efficiency, ease of manufacturing, and repeatability. This work presents a preliminary investigation on laser texturing of Ti6Al4 V alloy with a pulsed fiber laser source with the aim to increase surface adhesion for bonding. Particularly, different surface textures are proposed, and laser machining strategies are developed. The results showed that laser texturing provided up to eightfold and 30% higher shear strength compared to plain and sand blasted surfaces, respectively. Failure analysis showed that a margin of improvement is still possible by adapting the surface texture for better cavity filling and reducing surface damage caused by the laser treatment.

Purpose: This paper aims to investigate the processability by selective laser melting (SLM) of materials of potential interest for innovative biodegradable implants, pure Fe and pure Zn. The processability of these materials is evaluated with a more established counterpart in permanent implants, stainless steel. In particular, the processing conditions were studied to reduce porosity due to incomplete fusion of the powder. Design/methodology/approach: In the first phase of the experiments, SLM of AISI 316L was studied through design of experiments method. The study was used to identify the significant parameters in the experimental range and estimate the fluence ranges for pure Fe and pure Zn using the lumped heat capacity model. In the second phase, SLM of pure Fe and pure Zn were studied using estimated fluence ranges. In the final phase, best conditions were characterized for mechanical properties. Findings: The results showed that complete melting of AISI 316L and pure Fe could be readily achieved, whereas laser melting generated a foam-like porous structure in Zn samples. The mechanical properties of laser melt implant materials were compared to as-cast and rolled counterparts. Laser melted AISI 316L showed superior mechanical performance compared to as-cast and rolled material, whereas Fe showed mechanical performance similar to rolled mild steel. Despite 12 per cent apparent porosity, laser melted Zn exhibited superior mechanical properties compared to as-cast and wrought material because of reduced grain size. Originality/value: The paper provides key processing knowledge on the SLM processability of new biodegradable metals, namely, pure Fe, which has been studied sparingly, and pure Zn, on which no previous work is available. The results prefigure the production of new biodegradable metallic implants with superior mechanical properties compared to their polymeric counterparts and with improved degradation rates compared to magnesium alloys, the reference material for biodegradable metals.