In this paper, we report the extraction and characterization of gelatin from the abundant industrial fishery waste of Pangasius skin and swim bladder and its application as the base material for hard capsule shells. The yield of gelatin ranged between 19 and 23, content of moisture is 7.69.2, ash is 1.11.7, pH is 4.15.2, gel strength is 238278 bloom, and viscosity is 6574.7 mP. SDS-PAGE showed all gelatins have chains of α1, α2, and β-peptides. The skin, swim bladder, and mixed gelatins were successfully used in the production of hard capsule shells. The dimensions, weight, disintegration time, and water content properties of the hard capsules from these Pangasius wastes were akin to the standards of commercial capsules.

Dinding sel Ulva lactuca menghasilkan ulvan yang merupakan hidrokoloid bersulfat dan berpotensi sebagai antioksidan. Penelitian ini bertujuan untuk menentukan pengaruh lama pemanasan dalam autoklaf (15 dan 20 menit; 121℃) terhadap rendemen, kadar gula dan sulfat, serta aktivitas antioksidan ulvan. Rendemen ulvan, kandungan gula dan sulfat diukur masing-masing dengan metode gravimetri dan spektrofotometri. Ekstrak kering oven diuji gugus fungsi dan antioksidannya menggunakan FTIR dan metode DPPH. Ulvan hanya bisa dihasilkan melalui ekstraksi pada suhu 121℃ waktu 15 menit. Ekstrak kering ulvan memberikan rendemen 1,98%, kandungan gula total 46,06±0,16% dan kadar sulfat 21,53±1,16%. Spektrum FTIR menunjukkan adanya bilangan gelombang 850 dan 790 cm-1 yang merupakan ciri ulvan. Uji DPPH menghasilkan IC50 sebesar 469 ppm, yang tergolong sebagai antioksidan lemah.