Abundant biomass resources are a good choice for preparing electrode materials for supercapacitors, but developing a versatile and simple synthetic method to convert them into electrode materials remains a challenge. In the present research, our team reports a promising strategy and cost-efficient method to fabricate boron/sulfur-codoped porous carbon from biomass sources, mainly utilizing four biomass materials. Detailed material characterization showed that the samples produced by this approach possess rich B and S doping. Additionally, the original biomass materials treated by activation produce abundant pores. Therefore, owing to the synergetic effect of abundant atomic doping and microporous/mesoporous distribution, the obtained carbon as electrode material manifested excellent specific capacitances of 290 F g⁻¹ at a 0.5 A g⁻¹ current density. Moreover, the specific energy of the prepared samples of the as-assembled symmetric supercapacitor is as high as 16.65 Wh kg⁻¹ in 1 M Na₂SO₄, with a brilliant cyclical performance of only a 2.91% capacitance decay over 10,000 cycles. In addition, it has been verified universally that three other types of bio-wastes can also prepare electrode material using this method. This paper represents a significant attempt to turn waste biomass into treasure while also providing ideas for the design and preparation of supercapacitor electrode materials.

Polyurethane elastomers are anticipated to be applied in the field of cavitation erosion (CE) resistance, but their protection and damage mechanisms are not clear, which greatly restricts their further development. In this article, five polyether polyurethanes (PU_x) with different crosslinking densities were prepared. Their mechanical properties, thermal properties, water absorption, surface morphology and chemical structure before and after CE tests were compared with ESEM, OM, TG-DSC, FTIR and XPS in detail. The results showed that with an increase in crosslinking density, the tensile strength of PU_x increased first and then decreased, elongation at break and water absorption reduced gradually and thermal decomposition temperature and adhesion strength increased steadily. During the CE process, cavitation load aggravated the degree of microphase separation and made brittle hard segments concentrate on the coating surface; meanwhile, cavitation heat accelerated hydrolysis, pyrolysis, oxidation and the fracture of molecular chains. As a result, the mechano-thermal coupling intensified the formation and propagation of fatigue cracks, which should be the fundamental reason for the CE damage of polyurethane elastomer. PU_0.4 exhibited the best CE resistance among the five coatings thanks to its good comprehensive properties and may find potential applications on the surface of hydraulic components.

A novel acylhydrazone-based self-assembled supramolecular gel for ultrasensitive alternating fluorescence detection of Fe³⁺ and H₂PO₄⁻.

The first example of an acid-promoted difunctionalization of ketones to construct C–P and C–C bonds via a phospha-aldol-elimination is described under metal- and solvent-free conditions.

Recently, superhydrophobic surfaces with self-cleaning ability have attracted broad research interest due to their huge potential in daily lives and industrial applications, but the use of fluorinate, toxic organic compounds, and expensive feedstocks make superhydrophobic materials a great challenge in practical application. In this study, we present a facile dip-coating strategy to prepare superhydrophobic coatings with self-cleaning properties based on a non-fluorine and non-toxic system by using eco-friendly corn straw as raw material. During this process, aromatic carbon particles with rough hierarchical structures were prepared firstly via a simple fast pyrolysis process, followed by modification with polydimethylsiloxane (PDMS) in absolute ethanol solvent to decrease the surface free energy. Research shows these natural straw-derived carbons display a microstructure of several protrusions which is similar to the lotus leave’s and the resulted coatings exhibit an outstanding superhydrophobic property with a static water contact angle (WCA) of 151.67 ± 1.36 degrees. In addition, the as-prepared coatings possessed excellent self-cleaning performance: no contaminations were observed on the surfaces after examining with sludge, calcimine, water, and common liquids such as tea, milk, soybean milk as well as ink, which have a broad range of potential application in the field of antifouling, waterproofing, and anticorrosive.