A greater understanding of moisture sorption behaviour of aged wooden structural components, which has a close relationship with dimensional stability, is required to effectively evaluate and preserve historical artefacts. This study focused on the effects of aging on Baotou beam samples from a Chinese historical wooden building. An analysis of the sorption isotherms and hysteresis loops of a naturally aged, decayed sample (AOS), an aged sound sample (AIS), and a reference sample (RS), using classical sorption isotherm models revealed that the moisture sorption behaviour of samples from the same growth ring in a Baotou beam can differ significantly. AOS showed higher hygroscopicity than AIS, and both these samples were more hygroscopic than RS. Furthermore, the mono/multilayer moisture contents of AOS were always higher than those of AIS and RS. In addition, Fourier transform infrared, second-derivative infrared, and two-dimensional correlation infrared spectroscopy were used to investigate chemical changes in the samples. The relative hemicellulose and lignin contents of the samples changed significantly with wood aging. Furthermore, AOS exhibited the highest calcium oxalate content, which may be associated with fungal infections. Overall, these results provide valuable insights into the effects of aging on wood samples and the dimensional stability of timber structures, which could inform future research on methods for the preservation or restoration of aging timber structures.

Tetraethoxysilane (TEOS) is the most commonly used silicon-based reinforcement agent for conserving art relics due to its cost-effectiveness and commercial maturity. However, the resulting silica gel phase is prone to developing cracks as the gel shrinks during the sol–gel process, potentially causing severe damage to the objects being treated. In this study, dodecyltrimethoxysilane (DTMS) was introduced into TEOS to minimize this shrinkage by adding elastic long chains to weaken the capillary forces. The gel formed from the DTMS/TEOS hybrid material was transparent and crack-free, featuring a dense microstructure without mesopores or micropores. It exhibited excellent thermal stability, with a glass transition temperature of up to 109.64 °C. Evaluation experiments were conducted on artificially aged, handmade bamboo paper. The TEOS-based hybrid material effectively combined with the paper fibers through the sol–gel process, polymerizing into a network structure that enveloped the paper surface or penetrated between the fibers. The surface of the treated paper displayed excellent hydrophobic properties, with no significant changes in appearance, color, or air permeability. The mechanical properties of the treated bamboo paper improved significantly, with longitudinal and transverse tensile strengths increasing by up to 36.63% and 44.25%, respectively. These research findings demonstrate the promising potential for the application of DTMS/TEOS hybrid materials in reinforcing paper relics.

Palm leaf manuscripts are a valuable part of world cultural heritage. Studying the mechanical properties of palm leaf manuscripts and their changes due to environmental influences is of great significance for understanding the material characteristics, aging mechanisms, and preventive conservation of these manuscripts. This study used dynamic vapor sorption (DVS) and a thermomechanical analyzer (TMA) to investigate the changes to the mechanical properties of palm leaf manuscripts in response to different relative humidity conditions and different time periods. The short-term study results show that exposure to varying relative humidities leads to changes in the equilibrium moisture content (EMC) of palm leaf manuscripts, causing the bending strength of the samples to decrease significantly with increasing humidity. The bending modulus initially increases and then decreases as the humidity increases. Moreover, the greater the desorption hysteresis of the samples, the more pronounced the changes to the mechanical properties. Therefore, a stable environment in terms of humidity can prevent changes in the mechanical properties of palm leaf manuscripts, thereby preventing the onset of degradation. The results of the long-term aging studies indicate that prolonged exposure to either very dry or very humid conditions greatly affects the mechanical properties of palm leaf manuscripts, which is detrimental to their preservation. The samples kept at 50% RH did not exhibit significant signs of deterioration, with no notable changes in their mechanical properties or chemical structure. This suggests that 50% RH is a relatively optimal humidity condition for the preservation of palm leaf manuscripts.

Many degradation processes of cultural heritage objects are associated with unsuitable microclimatic conditions. One of the most ubiquitous deteriorations is the crystallization of salts in pores, which can accelerate the erosion rate of masonry historical relics. In this study, the microclimate of the burial tomb and exfoliation of sandstone in the Yongling Mausoleum of the Former Shu Dynasty in Chengdu were monitored for 1 year to determine the development of the degradation. We established a connection between the monitoring data and exfoliation variations of the stone with time. To predict the deterioration of the stone, a three-dimensional computational finite element model was used to simulate the detailed process of the thermo-hygrometric performance that led to salt crystallization and artwork deterioration. Two results were obtained. In the simulation of the microclimate, the temperature ranged from 15 to 22.6 °C, and the relative humidity was heterogeneous and varied between 60 and 100%. The other was the relationship between the microclimate and exfoliation. It was found that the exfoliation was more severe in the higher relative humidity areas where the water vapor frequently interacted with the relics. The crystallization and hydration of sulfate produced stress, which damaged the stone relics. These results provide a rationale analysis and a reference for better management of the environmental interactions and reduction of the environmental impacts in the subsequent scientific conservation of ancient Chinese cultural relics in tombs.

Palm Leaf Manuscripts represent a significant component of the world’s cultural heritage. Investigating their primary chemical components and understanding the transformations these materials undergo under environmental influences are crucial for elucidating their material characteristics and aging mechanisms and developing effective strategies for preventive conservation. This study utilized infrared absorption spectroscopy and X-ray diffraction analysis to examine changes in the primary chemical components of Palm Leaf Manuscripts under varying relative humidity conditions over extended periods. The findings reveal that dry environments lead to surface cracking, while humid environments promote mold growth, both of which contribute to the degradation of the primary chemical components. These degradative processes reduce cellulose crystallinity and thermal stability. The deterioration is particularly severe under high humidity, with hemicellulose degrading faster and more extensively than cellulose under the same conditions. After 200 days of aging at 10% RH and 90% RH, cellulose degradation reached 19.82% and 54.40%, respectively, while hemicellulose degradation was 34.78% and 64.28%. Correspondingly, the relative crystallinity of cellulose decreased by 8.01% and 13.11%. In contrast, samples maintained at 50% RH exhibited minimal deterioration, with cellulose and hemicellulose degrading by only 4.08% and 13.55%, respectively, and a 6.61% reduction in cellulose crystallinity. These results suggest that a relative humidity of 50% is optimal for the preservation of Palm Leaf Manuscripts. This study offers significant insights into the ageing mechanisms and preventive conservation of Palm Leaf Manuscripts, as well as other cellulose-based organic heritage materials.

The Dingtao M2 tomb, the largest and best-preserved imperial “Huangchangticou” tomb in China, holds great significance for its conservation. Currently, varying degrees of microbial degradation are occurring on the surfaces of the M2 tomb. This study aimed to determine the microbial diversity of the M2 tomb and its surrounding environment during July 2021 and August 2022. High-throughput metagenomic sequencing revealed that the dominant fungus on the surface of the tomb chamber was Dacrymyces stillatus (DTT1) in July 2021, which changed to Talaromyces pinophilus (DTT2) in August 2022. Enzymatic activities for cellulose and lignin degradation suggested that DTT1 has high levels of manganese peroxidase, lignin peroxidase, laccase, and cellulase. The wood of the tomb contained higher levels of Fe²⁺ and Ca²⁺, and experiments with different concentration gradients of these ions in the culture medium revealed that DTT1 exhibited greater activity of cellulose and lignin degradation in environments with higher concentrations of Fe²⁺ and Ca²⁺. DTT2 degraded both cellulose and lignin. Lastly, a laboratory plate inhibition experiment demonstrated that isothiazolinone fungicide had a significant fungicidal effect on these two dominant fungi. This study provides valuable data and a theoretical basis for the preservation of the M2 tomb and other wooden cultural relics.