In this study, high-performance modified biochar/alginate composite bead (MCB/ALG) adsorbents were prepared from recycled agricultural waste corncobs by a high-temperature pyrolysis and KOH/FeCl₃ activation process. The prepared MCB/ALG beads were tested for the adsorption of methylene blue (MB) dye from wastewater. A variety of analytical methods, such as SEM, BET, FTIR and XRD, were used to investigate the structure and properties of the as-prepared adsorbents. The effects of solution pH, time, initial MB concentration and adsorption temperature on the adsorption performance of MCB/ALG beads were discussed in detail. The results showed that the adsorption equilibrium of MB dye was consistent with the Langmuir isothermal model and the pseudo-second-order kinetic model. The maximum adsorption capacity of MCB/ALG−1 could reach 1373.49 mg/g at 303 K. The thermodynamic studies implied endothermic and spontaneous properties of the adsorption system. This high adsorption performance of MCB/ALG was mainly attributed to pore filling, hydrogen bonding and electrostatic interactions. The regeneration experiments showed that the removal rate of MB could still reach 85% even after five cycles of experiments, indicating that MCB/ALG had good reusability and stability. These results suggested that a win-win strategy of applying agricultural waste to water remediation was feasible.

A novel pyridine-modified chitosan (PYCS) adsorbent was prepared in a multistep procedure including the successive grafting of 2-(chloromethyl) pyridine hydrochloride and crosslinking with glutaraldehyde. Then, the as-prepared materials were used as adsorbents for the removal of metal ions from acidic wastewater. Batch adsorption experiments were carried out to study the impact of various factors such as solution pH value, contact time, temperature, and Fe (III) concentration. The results showed that the absorbent exhibited a high capacity of Fe (III) and the maximum adsorption capacity was up to 66.20 mg/g under optimal experimental conditions (the adsorption time = 12 h, pH = 2.5, and T = 303 K). Adsorption kinetics and isotherm data were accurately described by the pseudo-second-order kinetic model and Sips model, respectively. Thermodynamic studies confirmed that the adsorption was a spontaneous endothermic process. Moreover, the adsorption mechanism was investigated using Fourier transform infrared spectroscopy (FTIR) and X-ray photoelectron spectroscopy (XPS). The results revealed the pyridine group forms a stable chelate with iron (III) ions. Therefore, this acid-resistant adsorbent exhibited excellent adsorption performance for heavy metal ions from acidic wastewater compared to the conventional adsorbents, helping realize direct decontamination and secondary utilization.

Chitosan was used as the raw material. A quaternization reaction was carried out between 2,3-epoxypropyltrimethylammonium chloride and water-soluble chitosan to prepare quaternary ammonium salt water-soluble chitosan (QWSC), and its corrosion inhibition performance against the corrosion of carbon steel in stone processing wastewater was evaluated. The corrosion inhibition efficiencies of QWSC on carbon steel in stone processing wastewater were investigated through weight loss, as well as electrochemical and surface morphology characterization techniques. The results show that QWSC has superior corrosion inhibition performance for A3 carbon steel. When an amount of 60 mL·L⁻¹ is added, the corrosion inhibition efficiency can reach 59.51%. Electrochemical research has shown that a QWSC inhibitor is a mixed-type corrosion inhibitor. The inhibition mechanisms of the QWSC inhibitor revealed that the positive charge on the surface of carbon steel in stone wastewater was conducive to the adsorption of Cl⁻ in the medium, which produced an excessive negative charge on the metal’s surface. At the same time, the quaternary ammonium cation and amino cation formed in QWSC in stone processing wastewater can be physically absorbed on the surface of A3 carbon steel, forming a thin-film inhibitor to prevent metal corrosion.

It has been proven that the gas trifluoromethanesulfonyl fluoride (CF₃SO₂F) has good dielectric performance and the potential to replace the potent greenhouse gas sulfur hexafluoride (SF₆), which is the most commonly used insulating gas in high-voltage electrical equipment. However, there are many key biochemical properties, such as toxicity, that the new eco-friendly insulating gas will need to obtain. It could protect the operator and equipment and help the chemical engineering development of this gas in the power grid industry. In this study, according to Horn’s method, an acute toxic gas inhalation test was carried out. The results showed that the lethal concentration of 50% (LC50) for female rats was 27.1 g/m³, and that for male rats was 23.3 g/m³. The behavioral and vital sign changes in the rats were recorded. Pathological sections of the main organs revealed that the heart, lungs, spleen, and eyes suffered the most damage from the gas. This research also provides scientific suggestions for the protection of electrical workers exposed to the insulating gas CF₃SO₂F.