The healing of complex diabetic wounds with a hyperglycemic microenvironment and bacterial infection is considered an important clinical issue. In this study, glucose oxidase (GOx) and gold nanoclusters (AuNCs) were encapsulated in quaternary carboxymethyl chitosan (QCMCS)/sodium alginate oxide (OSA) hydrogels and were immersed in tannic acid (TA) solution to achieve antioxidant, antibacterial, pro-angiogenesis, pro-collagen deposition and real-time monitoring functions. In vitro studies showed that TA-QCMCS/OSA@GOx@AuNC hydrogels had inhibition rates of 98.99% and 99.99% against S. aureus and E. coli, respectively, and the survival rate of mouse fibroblasts (L929) was over 95%. In vivo studies showed that TA-QCMCS/OSA@GOx@AuNC hydrogels were 97.28% effective in healing diabetic wounds. In addition, image signals from TA-QCMCS/OSA@GOx@AuNC hydrogels can be collected in real time to accurately obtain glucose concentration values of diabetic wounds and reflect the healing status of diabetic wounds in a timely manner. The results showed that TA-QCMCS/OSA@GOx@AuNC hydrogels provide a novel idea for real-time monitoring of diabetic wound treatment.

Bacterial infections have a serious impact on public health. It is urgent to develop antibacterial hydrogels with good biocompatibility to reduce the use of antibiotics. In this study, poly(lipoic acid-co-sodium lipoate)–phytic acid (P(LA-SL)-PA) hydrogels are prepared by a simple mixture of the natural small molecules lipoic acid (LA) and phytic acid (PA) in a mild and green reaction environment. The crosslinking network is constructed through the connection of covalent disulfide bonds as well as the hydrogen bonds, which endow the injectable and self-healing properties. The P(LA-SL)-PA hydrogels exhibit an adjustable compression modulus and adhesion. The in vitro agar plates assay indicates that the antibacterial rate of hydrogels against Escherichia coli and Staphylococcus aureus is close to 95%. In the rat-infected wound model, the P(LA-SL)-PA hydrogels adhere closely to the tissue and promote epithelialization and collagen deposition with a significant effect on wound healing. These results prove that the P(LA-SL)-PA hydrogels could act as effective wound dressings for promoting the healing of infected wounds.

After traditional osteosarcoma resection, recurrence of tumor is still a major clinical challenge. The combination of chemotherapy and photothermal therapy (PTT) has great potential in improving therapeutic effect. However, the studies using polydopamine (PDA) as photothermal transducing agent to improve the anti-cancer activity of curcumin (CM)-loaded poly (l-lactic acid) (PLLA) microparticles (PLLA/CM) have seldom been investigated. In this study, we reported the synthesis of PDA-coated PLLA/CM microparticles (PDA-PLLA/CM) prepared by PDA coating on the surface of the PLLA/CM microparticles fabricated by solution-enhanced dispersion by supercritical CO₂ (SEDS) for chemo-photothermal therapy of osteosarcoma. The average particle sizes of PLLA/CM and PDA-PLLA/CM microparticles with a spherical shape were (802.6 ± 8.0) nm and (942.5 ± 39.5) nm, respectively. PDA-PLLA/CM microparticles exhibited pH- and near-infrared (NIR)-responsive release behavior to promote CM release in the drug delivery system. Moreover, PDA-PLLA/CM microparticles displayed good photothermal conversion ability and photothermal stability attributed to PDA coating. Additionally, the results of in vitro anti-cancer experiment showed that 500 μg/mL PDA-PLLA/CM microparticles had good anti-cancer effect on MG-63 cells and no obvious toxicity to MC3T3-E1 cells. After incubation with PDA-PLLA/CM microparticles for 2 days, NIR irradiation treatment improved the anti-cancer activity of PDA-PLLA/CM microparticles obviously and reduced the cell viability of osteosarcoma from 47.4% to 20.6%. These results indicated that PDA-PLLA/CM microparticles possessed a synergetic chemo-photothermal therapy for osteosarcoma. Therefore, this study demonstrated that PDA-PLLA/CM microparticles may be an excellent drug delivery platform for chemo-photothermal therapy of tumors.