The primary objective of this research was to study the transmission of gamma radiation from heavyweight concrete containing barite aggregates. For this purpose, cylindrical and cubic specimens were produced for 10 mix designs. The mix designs containing different percentages of barite aggregates were calculated; five mix designs were also calculated for the compressive strength of 25 MPa, while five of them were designed for the compressive strength of 35 MPa to study the influence of the compressive strength rate on the reduction in gamma radiation transmission. The results indicated that both compressive and tensile strength was decreased by increasing the ratio of barite aggregates. The rate in reduction of compressive strength and especially tensile strength in concrete C35 was less than in concrete C25. The use of barite aggregates increased the attenuation coefficient of concrete. The attenuation coefficient in C35 concrete increased more than that in C25 upon increasing the amount of barite aggregate. By increasing the thickness of concrete with different percentages of barite, the rate of radiation loss in different samples was closer. The difference in the rate of radiation loss at a thickness of 150 mm was not much different from that at a thickness of 100 mm, whereas it was considerably decreased at a thickness of 300 mm. The test results indicated that the reduction in the gamma transmission rate is significantly dependent on the density of concrete.