The present study aimed to optimize the electrospinning parameters for polyacrylonitrile (PAN) nanofibers containing MgO nanoparticle to obtain the appropriate fiber diameter and mat porosity to be applied in air filtration. Optimization of applied voltage, solution concentration, and spinning distance was performed using response surface methodology. In total, 15 trials were done according to the prepared study design. Fiber diameter and porosity were measured using scanning electron microscopic (SEM) image analysis. For air filtration testing, the nanofiber mat was produced based on the suggested optimum conditions for electrospinning. According to the results, the lower solution concentration favored the thinner fiber. The larger diameter gave a higher porosity. At a given spinning distance, there was a negative correlation between fiber diameter and applied voltage. Moreover, there were curvilinear relationships between porosity and both spinning distance and applied voltage at any concentration. It was also concluded that the developed filter medium could be comparable to the high-efficiency particulate air (HEPA) filter in terms of collection efficiency and pressure drop. The empirical models presented in this study can provide an orientation to the subsequent experiments to form uniform and continuous nanofibers for future application in air purification. Implications: High-efficiency filtration is becoming more important, due to decreasing trends air quality. Effective filter media are increasingly needed in industries applying clean-air technologies, and the necessity for developing the high-performance air filters has been more and more felt. Nanofibrous filter media that are mostly fabricated via electrospinning technique have attracted considerable attention in the last decade. The present study aimed to develop the electrospun PAN-containing MgO nanoparticle (using the special functionalities such as absorption and adsorption characteristics, antibacterial functionality, and as a pore-forming agent) filter medium through experimental investigations for application in high-performance air filters.

Introduction. This article aimed to investigate the effect of heat stress on cognitive performance and the blood concentration of stress hormones among workers of a foundry plant. Methods. Seventy workers within the exposed (35 people) and unexposed (35 people) groups were studied. The wet bulb globe temperature (WBGT) index was measured for heat stress assessment. The cognitive performance tests were conducted using the Stroop color word test (SCWT) before and during working hours. For the assessment of the serum level of cortisol and the plasma level of adrenaline and noradrenaline, blood samples were taken during working hours from both groups. Results. Only for SCWT III was there a significant relationship between heat stress and test duration, error rate and reaction time. The laboratory test results revealed significantly higher concentrations of cortisol, adrenaline and noradrenaline in the exposed subjects than in the unexposed group. There existed a positive correlation between cortisol, adrenaline, noradrenaline and WBGT index and also test duration and reaction time of SCWT III, and number of errors of SCWT I, SCWT II and SCWT III during work. Conclusion. Heat stress can lead to an increase in the blood level of stress hormones, resulting in cognitive performance impairment.

This study was conducted to investigate the heat stress and semen quality among male workers in a steel industry in Iran and investigate the relationship between heat stress indices and semen parameters. The study was conducted on workers exposed (n = 30) and unexposed (n = 14) to heat in a steel industry. After obtaining a brief biography of the selected employees, scrotal temperature, oral temperature, and environmental parameters were measured, and their semen samples were analyzed according to the procedure recommended by the World Health Organization. The heat stress indices, including wet-bulb globe temperature (WBGT) and predicted heat strain (PHS), in their workplace were calculated according to environmental parameters (ISO 7243:1989 and 7933:2004, respectively). Time-weighted averages of WBGT and PHS (35.76°C and 491.56 w/m2wm2 , respectively) for the exposed group were higher than threshold limit values. The mean difference of environmental, physiological, and semen parameters (exception: pH of semen), and also WBGT and PHS indices were statistically significant (p < 0.05) between the two groups. Mean semen parameters were in the normozoospermic range. WBGT and PHS indices showed significantly "negative" correlation with physiological parameters (scrotal and oral temperature) and most semen parameters (semen volume, sperm morphology, sperm motility, sperm count; p < 0.05); moreover, the correlation of WBGT with these parameters was stronger than PHS. Semen parameters of the studied workers exposed to heat were in the borderline level of normozoospermic range, and their semen parameters were significantly lower than controls. For better assessment of occupational environment concerning physiological and semen parameters in steel industries, WBGT can be a more useful index.

The present study aimed to investigate the applicability of Universal Thermal Climate Index (UTCI) as an innovative and science-based index in public health researches, in occupational heat stress assessment. All indoor and outdoor workers (200 people) of Brick industries of Shahroud, Iran participated in the research. First, the environmental variables such as air temperature, wet-bulb temperature, globe temperature, air velocity and relative humidity were measured; then UTCI and WBGT (wet-bulb globe temperature) indices were calculated. Simultaneously, physiological parameters including systolic and diastolic blood pressure, oral temperature, skin temperature, tympanic temperature and heart rate of workers were measured. UTCI and WBGT indices were 34.2 ± 2°C, 21.8 ± 1.8°C in the outdoor environments and 38.1 ± 4.4°C, 24.7 ± 3.3°C at the indoor environments, respectively. There were the weak inverse relationships between UTCI and WBGT indices at the outdoor environments and physiological responses such as systolic blood pressure, and diastolic blood pressure. However, there were no similar results for indoor environments. The significant relationships were found between UTCI and WBGT at both indoor and outdoor environments. Both UTCI and WBGT indices are suitable for assessing the occupational heat stress. Although, UTCI index seems more appropriate for heat stress assessment in the environments with low humidity and air velocity.

The main purpose of this study was to evaluate the ultraviolet protective factor (UPF) of fabrics coated with TiO2 nanoparticles made using anin-situsynthesis method and more accurately assess the intrinsic properties of the textile. The cotton-polyester twill fabric (70–30%) (246.67 g/m2) was coatedin-situwith TiO2 nanoparticles.In-situcoating is conducted in 4 steps; washing the fabrics, preparation of nanoparticles, injecting the nanoparticles into fabrics, and drying the fabric after coating. The scanning electron microscope (SEM) and X-ray diffraction (XRD), FTIR spectrometer, dynamic light scattering (DLS) and UV-Vis spectrophotometer were used to analyse the data of the coating and UPF results. Also, four standards such as ASTM D737, ISIRI 8332, ISIRI 4199, and ISIRI 567 were used for analyzing the intrinsic properties of a textile. The results of SEM, XRD and DLS altogether confirmed thein-situformation of nanoparticles onto textile fibers. Moreover, the UPF value of the uncoated and coated fabrics was 3.67 and 55.82, respectively. It was shown that thein-situdeposition of TiO2 nanoparticles on fabric can provide adequate protection against UVR. Also, the results of analyzing the intrinsic properties of the textile showed that there were no significant differences in the intrinsic properties between the coated and uncoated fabrics. Based on the results, it can be concluded that the UV protective properties of workwear fabrics can be improved by coating TiO2 nanoparticles on them without any effect on the cooling effect of perspiration evaporation.