The Black Steel slag (Ss) and phosphogypsum (PG) are industrial wastes produced in Morocco. In order to reduce these two wastes and to evaluate their pozzolanic reactivity in the presence of water, they were incorporated into bentonite (B) mixed with lime (L). The studied mixtures (BLW, BL–PG–W and BL–PG–Ss–W) were analyzed by X-ray diffraction, Infrared spectroscopy, Raman spectroscopy and SEM/EDX analysis. Compressive strength tests were performed on hardened specimens. The results obtained show that the hydration kinetics of the B–L–W and B–L–PG–W mixtures are slow. The addition of PG to a bentonite––lime mixture induces the formation of new microstructures such as hydrated calcium silicate (C–S–H) and ettringite, which increases the compressive strength of the cementitious specimens. The addition of the Ss to a mixture composed of 8%PG and 8%L–B accelerates the kinetics of hydration and activates the pozzolanic reaction. The presence of C₂S in the slag helps to increase the mechanical strength of the mixture B–L–PG–Ss. The compressive strength of the mixtures BL–W, BL–PG–W and BL–PG–Ss–W increases from 15 to 28 days of setting. After 28 days of setting, 8% of Sc added to the mixture 8% PG–8%L–B is responsible for an increase of the compressive strength to 0.6 MPa.

Waste recycling with increasing the lifecycle of resource is a novel approach for enhancing circular economy. Within this context, this study aims to give a second life cycle to phosphogypsum (PG) waste, which is a by-product from phosphoric acid manufacture, as useful resources. This study evaluates the sustainability of this harmful waste, which is accumulated in large stockpiles and becomes hazardous during storage, and to stabilize bentonite-based concrete intended for road construction.The effect of raw bentonite (Ca-Na montmorillonite), PG, and lime on the properties of cementitious materials has been investigated through various tests. The properties examined include chemistry (X-ray Fluorescence Spectrometry), mineralogy (X-ray Powder Diffraction and Fourier-Transform Infrared Spectroscopy), calorimetry (Differential Thermal Analysis/Thermogravimetry) and microstructure (Scanning Electron Microscopy) of the mortar based on different mixtures of bentonite, PG and lime. The result show that lime and PG addition involves in the formation of new nanocrystalline phases and the disappearance of certain minerals as portlandite. Calcium silicate hydrate gel appeared in the mixture with 8% of lime, whereas strätlingite was neoformed in the mixture with 8% of lime and 8% of PG. These nanocrystalline phases are responsible for enhancing mechanical strength through the pozzoloanic reaction.