Microbial cells secrete extracellular polymeric substances (EPS) to adhere to material surfaces, if they get in contact with solid materials such as metals. After phase equilibrium, microorganisms can adhere firmly to the metal surfaces causing metal dissolution and corrosion. Attachment and adhesion of microorganisms via EPS increase the possibility and the rate of metal corrosion. Many components of EPS are electrochemical and redox active, making them closely related to metal corrosion. Functional groups in EPS have specific adsorption ability, causing them to play a key role in biocorrosion. This review emphasizes EPS properties related to metal corrosion and protection and the underlying microbially influenced corrosion (MIC) mechanisms. Future perspectives regarding a comprehensive study of MIC mechanisms and green methodologies for corrosion protection are provided.

Microorganisms that exist in the seawater form microbial biofilms on materials used in marine construction, especially on metal surfaces submerged in seawater, where they form biofilms and cause severe corrosion. Biofilms are mainly composed of bacteria and their secreted polymeric substances. In order to understand how biofilms promote metal corrosion, planktonic and biofilm cells of Desulfovibrio bizertensis SY-1 (D. bizertensis) from Q235 steel were collected and analyzed as to their intracellular proteome and extracellular polymeric substances (EPS). The intracellular proteome analysis showed that the cellular proteins were strongly regulated in biofilm cells compared to planktonic cells, e.g., along with flagellar proteins, signaling-related proteins were significantly increased, whereas energy production and conversion proteins and DNA replication proteins were significantly regulated. The up-and-down regulation of proteins revealed that biofilm formation by bacteria on metal surfaces is affected by flagellar and signaling proteins. A significant decrease in DNA replication proteins indicated that DNA is no longer replicated and transcribed in mature biofilms, thus reducing energy consumption. Quantitative analysis and lectin staining of the biofilm on the metal’s surface revealed that the bacteria secreted a substantial amount of EPS when they began to attach to the surface, and proteins dominated the main components of EPS. Further, the infrared analysis showed that the secondary structure of the proteins in the EPS of the biofilm was mainly dominated by β-sheet and 3-turn helix, which may help to enhance the adhesion of EPS. The functional groups of EPS analyzed using XPS showed that the C element of EPS in the biofilm mainly existed in the form of combinations with N. Furthermore, the hydroxyl structure in the EPS extracted from the biofilm had a stronger hydrogen bonding effect, which could maintain the stability of the EPS structure and biofilm. The study results revealed that D. bizertensis regulates the metabolic pathways and their secreted EPS structure to affect biofilm formation and cause metal corrosion, which has a certain reference significance for the study of the microbially influenced corrosion (MIC) mechanism.

The effects of medium and flow rate on the film-forming structures of B10 Cu-Ni alloys and their resistance to corrosion caused by sulfate-reducing bacteria are investigated in this article. Combined with a predicted cloud map of pipeline corrosion area and a particle motion trajectory map obtained using Computational Fluid Dynamics (CFD), the growth law of alloy passivation films was analyzed and the pitting process of sulfate-reducing bacteria (SRB) on passivation films was revealed. The results show that the film formation effect is best when the stream of water in the film-forming environment is filtered seawater with a flow rate of 0.8 m/s, which consists of a uniform and dense gray-brown passivated film layer with the strongest resistance to SRB corrosion. When the flow rate is 0 m/s, the clay particles in the seawater cover the surface of the passivation film, hindering the contact of oxygen with the substrate and inhibiting the growth of the passivation film. When the stream of water in the film-forming environment is seawater with a flow rate of 3 m/s, the surface of the substrate shows obvious scouring marks, which is favorable for the enrichment of SRB and further accelerates the pitting corrosion of the substrate. Cl⁻ has a significant influence on the formation of passivation films on B10 Cu-Ni alloys. When the filming medium is deionized water, the B10 Cu-Ni alloy does not form a complete passivation film at all flow rates.