The food industry produces large amounts of solid and also liquid wastes. Different waste materials and their mixtures were pyrolysed in the laboratory pyrolysis unit to a final temperature of 800°C with a 10 minute delay at the final temperature. After the pyrolysis process of the selected wastes a mass balance of the resulting products, off-line analysis of the pyrolysis gas and evaluation of solid and liquid products were carried out. The highest concentration of methane, hydrogen and carbon monoxide were analyzed during the 4th gas sampling at a temperature of approx. 720–780°C. The concentration of hydrogen was measured in the range from 22 to 40 vol.%. The resulting iodine numbers of samples CHFO, DS, DSFW reach values that indicate the possibility of using them to produce the so-called “disposable sorbents” in wastewater treatment. The WC condensate can be directed to further processing and upgrading for energy use.

The large and growing volume of tire waste and sewage sludge requires disposal, for which thermochemical processes such as gasification can be used. Co-gasification of these two waste products allows the tire char to be used as a charge stabilizer and the sewage sludge to improve reactivity and efficiency. The purpose of this study was to evaluate the effect of the composition of a waste tire char and sewage sludge fuel blend on the gasification process, using steam as the gasification agent. Tests were carried out for tire char, municipal sewage sludge, and blends of the two in ratios of 90:10 and 67:33. An analysis of the materials used was carried out (ultimate and proximate analysis as well as ash composition), and isothermal measurements of steam gasification were taken using the thermal volumetric method for temperatures of 800, 850, and 900 °C at an elevated pressure of 1 MPa. On the basis of the results, the formation curves of the main gasification products (H₂, CO, CO₂, and CH₄) were created, the curves for the degree of carbon conversion were plotted, the reactivity indexes were determined for different degrees of conversion (0.25, 0.5, and 0.75), and the quantity and composition of the resulting gas were analyzed. Using the grain model, the kinetic parameters (activation energy and pre-exponential factor) of the gasification reaction were calculated. The addition of municipal sewage sludge had a positive effect on the reactivity of tire char and increased the efficiency of gasification, because it contained components that act as catalysts in the gasification process. There was a favorable effect from the addition and higher amount of sewage sludge on lowering both the activation energy (49.5 kJ/mol and 89.2 kJ/mol for 90:10 and 67:33 blends, respectively) and the pre-exponential factor. A significant improvement in reactivity, with a high degree of conversion and the best gas composition, was obtained for a 90:10 blend at 900 °C.

Waste from the Miscanthus production cycle may be a promising source of material for the pyrolysis and biochar production. The biochar can be used to enrich the soil on which the crop grows, thus increasing productivity. A sample of Miscanthus rhizomes was used as a raw material in a series of experiments in order to find the most suitable conditions for the preparation of biochar. Miscanthus biochar was prepared in a laboratory unit using four different temperatures (i.e., 400, 500, 600 and 700 °C). All pyrolysis products were subsequently evaluated in terms of their quality and product yields were determined. For a temperature of 600 °C and a residence time of 2 h, the appropriate properties of biochar were achieved and the process was still economical. The biochar contained a minimal number of polycyclic aromatic hydrocarbons and a high percentage of carbon. Surface area was measured to be 217 m²/g. The aqueous extract of biochar was alkaline.