In YBCO coils, the increased transport current density and magnetic field will induce larger electromagnetic force, and YBCO coated conductors (CCs) may suffer interlayer delamination by shear forces, which may give rise to performance degradation of the conductor. The delamination characteristics of YBCO CCs under shear stress should be well understood for better application of YBCO tapes to high-temperature superconducting equipment. This paper describes the experimental results for different delamination strength and critical current I _c degradation behaviors of the YBCO CCs under shear stress at the unslit edge, center, and slit edge of the conductor. The results show that the average delaminated shear strengths of 4.9, 5.9, and 3.7 MPa are recorded for the unslit edge, center, and slit edge at room temperature, whereas 6.8, 7.2, and 5.1 MPa are recorded for the unslit edge, center, and slit edge at liquid nitrogen. The different degradation behaviors of I _c under shear stress are related to the location where delamination occurs in the sample. According to the finite-element method analysis for the stress distribution of the conductor under shear stress, stress concentration leads to initial delamination of the conductor. The decrease of moment arm is suggested to reduce the effect of moment on the delamination test.

AC losses undoubtedly increase the burden on the cooling system and affect the overall performance of high-temperature superconducting (HTS) cables. Therefore, AC losses in HTS cables are important design factors for large-scale HTS equipments. Extensive research has been conducted on straight, densely wound conductors. However, AC losses of bending/circular HTS cable conductors have not been sufficiently studied. In this article, the transport AC losses in a circular HTS conductor coil bended by a conductor on round core (CORC) type cable were investigated using experiments and numerical simulations. The effect of different winding methods was also studied. First, the modeling method of the three-dimensional simulation and the experimental procedures were presented. The simulation results of the straight densely wound conductor (SDWC) and circular densely wound coil (CDWC) were compared with the corresponding experimental results. Finally, the winding method for the CDWC was optimized using both the simulation and experimental approaches. Both the experiments and simulations showed that reducing the tape-to-tape frontal area was able to decrease the transport AC loss, and the results show that the optimum winding angle of the HTS CORC coil was 24.15°. Overall, the modeling and experiments provide useful optimization strategies for designing winding structures of high-performance CORC coils/magnets.

The quench properties for REBCO conductor in SN ₂ and conduction cooled system are studied. The normal zone propagation velocity determined by voltage, temperature, and strain methods is compared to demonstrate the feasibility of strain method to detect the quench of the REBCO conductor.