This study compared the osseointegration of acid-etched, ultrahydrophilic, micro- and nanostructured implant surfaces (ANU) with non-ultra-hydrophilic, microstructured (SA) and non-ultrahydrophilic, micro- and nanostructured implant surfaces (AN) in vivo. Fifty-four implants (n = 18 per group) were bilaterally inserted into the proximal tibia of New Zealand rabbits (n = 27). After 1, 2, and 4 weeks, bone-implant contact (BIC, %) in the cortical (cBIC) and spongious bone (sBIC), bone chamber ingrowth (BChI, %), and the supra-crestal, subperiosteal amount of newly formed bone, called percentage of linear bone fill (PLF, %), were analyzed. After one week, cBIC was significantly higher for AN and ANU when compared to SA (p = 0.01 and p = 0.005). PLF was significantly increased for ANU when compared to AN and SA (p = 0.022 and p = 0.025). After 2 weeks, cBIC was significantly higher in SA when compared to AN (p = 0.039) and after 4 weeks, no significant differences in any of the measured parameters were found anymore. Ultrahydrophilic implants initially improved osseointegration when compared to their non-ultrahydrophilic counterparts. In accordance, ultrahydrophilic implants might be appropriate in cases with a necessity for an accelerated and improved osseointegration, such as in critical size alveolar defects or an affected bone turnover.

Ultrahydrophilic titanium miniplates with sandblasted and acid etched (SLA) surfaces were protected from loss of hydrophilicity by an exsiccation layer of salt and stored in a dry state. Various salts in different concentrations were tested in respect to their conservation capacity and optical appearance. Potassium phosphate buffer in a specified composition appeared to be optimal. This optimal system was applied in a long time storage experiment showing no loss of hydrophilicity over years. It was also transferred with success to hyperhydrophilic dental implants.