Self-assembly of particles into long-range, three-dimensional, ordered superstructures is crucial for the design of a variety of materials, including plasmonic sensing materials, energy or gas storage systems, catalysts and photonic crystals. Here, we have combined experimental and simulation data to show that truncated rhombic dodecahedral particles of the metal–organic framework (MOF) ZIF-8 can self-assemble into millimetre-sized superstructures with an underlying three-dimensional rhombohedral lattice that behave as photonic crystals. Those superstructures feature a photonic bandgap that can be tuned by controlling the size of the ZIF-8 particles and is also responsive to the adsorption of guest substances in the micropores of the ZIF-8 particles. In addition, superstructures with different lattices can also be assembled by tuning the truncation of ZIF-8 particles, or by using octahedral UiO-66 MOF particles instead. These well-ordered, sub-micrometre-sized superstructures might ultimately facilitate the design of three-dimensional photonic materials for applications in sensing.

Adsorptive heat transformation systems such as adsorption thermal batteries and chillers can provide space heating and cooling in a more environmental friendly way. However, their use is still hindered by their relatively poor performances and large sizes due to the limited properties of solid adsorbents. Here, the spray‐drying continuous‐flow synthesis of a new type of solid adsorbents that results from combining metal‐organic frameworks (MOFs), such as UiO‐66, and hygroscopic salts, such as CaCl₂ has been reported. These adsorbents, commonly named as composite salt in porous matrix (CSPM) materials, allow improving the water uptake capabilities of MOFs while preventing their dissolution in the water adsorbed; a common characteristic of these salts due to the deliquescence effect. It is anticipated that MOF‐based CSPMs, in which the percentage of salt can be tuned, are promising candidates for thermal batteries and chillers. In these applications, it is showed that a CSPM made of UiO‐66 and CaCl₂ (38% w/w) exhibits a heat storage capacity of 367 kJ kg⁻¹ , whereas a second CSPM made of UiO‐66 and CaCl₂ (53% w/w) shows a specific cooling power of 631 W kg⁻¹ and a coefficient of performance of 0.83, comparable to the best solid adsorbents reported so far.

Porous metal–organic frameworks (MOFs) are attracting great attention from industry, thanks to their myriad potential applications in areas such as catalysis and gas storage. Zr-MOFs (also known as UiO-type MOFs) are especially promising, owing to their large surface areas, high chemical versatility and remarkable hydrothermal, chemical and thermal stabilities. However, among the challenges currently precluding the industrial exploitation of MOFs is the lack of green methods for their synthesis. Herein we describe a continuous-flow spray-drying method for the simultaneous synthesis and shaping of spherical MOF microbeads in a mixture of water and acetic acid. We used this approach to build two archetypical Zr-MOFs: UiO-66-NH₂ and Zr-fumarate. By tuning the concentration of acetic acid in water, we were able to produce, by a scalable process, UiO-66-NH₂ and Zr-fumarate beads with S_BET and water-sorption values comparable to the literature values obtained with other methods.

Materials with surfaces that can be switched from high/superhydrophobicity to superhydrophilicity are useful for myriad applications. Herein, we report a metal–organic framework (MOF) assembled from Zn^II ions, 1,4‐benzenedicarboxylate, and a hydrophobic carborane‐based linker. The MOF crystal‐surface can be switched between hydrophobic and superhydrophilic through a chemical treatment to remove some of the building blocks.

Herein, we exploit the well‐known swelling behaviour of metal–organic frameworks (MOFs) to create a self‐folding polymer film. Namely, we show that incorporating crystals of the flexible MOF MIL‐88A into a polyvinylidene difluoride (PVDF) matrix affords a polymer composite film that undergoes reversible shape transformations upon exposure to polar solvents and vapours. Since the self‐folding properties of this film correlate directly with the swelling properties of the MIL‐88A crystals, it selectively bends to certain solvents and its degree of folding can be controlled by controlling the relative humidity. Moreover, it shows a shape‐memory effect at relative humidity values from 60 % to 90 %. As proof of concept, we demonstrate that these composite films can lift cargo and can be used to assemble 3D structures from 2D patterns. Our strategy is a straightforward method for designing autonomous soft materials with folding properties that can be tuned by judicious choice of the constituent flexible MOF.