Different nanostructures (Ns), such as nanobelts, nanobricks and nanosheets, of polypyrrole (PPy) were successfully fabricated on stainless steel substrates by simply varying the scan rate of deposition in the potentiodynamic mode. These PPy Ns were characterized using X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM), and surface area measurement. The XRD analysis showed the formation of amorphous PPy thin films, and the FTIR studies confirmed characteristic chemical bonding in the PPy materials. SEM images depicted that a high scan rate of deposition can form multilayer nanosheets with high porosity leading to a system with excellent processability. The PPy nanosheets possess a higher Brunauer–Emmett–Teller (BET) surface area of 37.1 m² g⁻¹ than PPy nanobelts and nanobricks. The supercapacitive performances of different PPy Ns were evaluated using cyclic voltammetry (CV) and galvanostatic charge–discharge techniques in 0.5 M H₂SO₄. A maximum specific capacitance of 586 F g⁻¹ was obtained for multilayer nanosheets at a scan rate of 2 mV s⁻¹. In addition, impedance measurements of the different Ns of PPy electrodes were performed suggesting that the PPy electrodes with multilayer nanosheets are promising materials for the next generation high performance electrochemical supercapacitors.

Electricity was produced by catalytic oxidation of carbon monoxide (CO) by using gold catalysts at room temperature. The observed rates are faster than conventional processes operating at 500 kelvin or higher for the conversion of CO with water to produce hydrogen and carbon dioxide through the water-gas shift (WGS). By eliminating the WGS reaction, we remove the need to transport and vaporize liquid water in the production of energy for portable applications. This process can use CO-containing gas streams from the catalytic reforming of hydrocarbons to produce an aqueous solution of reduced polyoxometalate compounds that can be used to generate power. The reduced polyoxometalate can be reoxidized in fuel cells that contain simple carbon anodes.