Freeze–thaw cycle is one of the main distresses of asphalt pavement, and the law of freeze–thaw damage has always been an important topic. In this paper, X-ray computed tomography (CT) of asphalt mixture before and after freezing and thawing was carried out, and its two-dimensional (2D) digital image was recognized. Firstly, the eigenvalues of internal voids of asphalt mixture are extracted. Then the distribution of internal voids was analyzed. Finally, the evolution law of internal voids was summarized. The research results show that the characteristic mean value of the 9th cycle is the irreversible limit of freeze–thaw damage, and the non-resilience after the large void area increases is the fundamental reason for the accumulation of freeze–thaw damage. The source of void damage shifts from large voids to small voids, and the middle-stage is a critical stage of freeze–thaw damage. This work quantitatively evaluates the internal freeze–thaw damage process of asphalt mixture, and a morphological theory of the evolution of void damage based on an equivalent ellipse is proposed, which is helpful for better understanding the freezing–thawing damage law of asphalt pavement.

The use of waste tires to prepare rubberized asphalt has been a hot trend in recent years, and the characteristics of adhesion between rubberized asphalt and aggregates are important factors affecting the performance of asphalt pavement. However, there is a lack of uniform results on the adhesion characteristics of rubberized asphalt. Therefore, crumb-rubber-modified asphalt (CRMA) with 15%, 20%, and 25% rubber contents was prepared in this work, and the basic rheological parameters and cohesive energy of the rubberized asphalt were characterized by DSR. The adhesion properties between rubberized asphalt and aggregates were characterized based on macroscopic binder bond strength (BBS), surface free energy (SFE) theory, and nanoscale atomic force microscopy (AFM) tests. The results show that crumb rubber (CR) can improve the high-temperature elastic properties of asphalt; secondly, CR can have a negative impact on the maximum tensile strength of asphalt and aggregates. CR can improve the SFE parameter of asphalt. The work of adhesion of rubberized asphalt and limestone is the highest, followed by basalt and, finally, granite. Finally, CR can cause the catanaphase in asphalt to gradually break down and become smaller, and the adhesion of rubberized asphalt can be reduced. Overall, CR can reduce the adhesion performance of asphalt, and this work provides a reference for the application of rubberized asphalt.