Because bone-associated diseases are increasing, a variety of tissue engineering approaches with bone regeneration purposes have been proposed over the last years. Bone tissue provides a number of important physiological and structural functions in the human body, being essential for hematopoietic maintenance and for providing support and protection of vital organs. Therefore, efforts to develop the ideal scaffold which is able to guide the bone regeneration processes is a relevant target for tissue engineering researchers. Several techniques have been used for scaffolding approaches, such as diverse types of biomaterials. On the other hand, metallic biomaterials are widely used as support devices in dentistry and orthopedics, constituting an important complement for the scaffolds. Hence, the aim of this review is to provide an overview of the degradable biomaterials and metal biomaterials proposed for bone regeneration in the orthopedic and dentistry fields in the last years.

The additive manufacturing (AM) technique can produce Ti-6Al-4V ELI (extra low interstitial) alloy for personalized biomedical devices. However, the Ti-6Al-4V ELI alloy presents poor tribological behavior. Regarding this, coatings are a feasible approach to improve the wear resistance of this alloy. In the literature, the tribological behavior of TiO₂ coatings incorporated with Ca and P formed by one-step plasma electrolytic oxidation (PEO) on Ti-6Al-4V ELI alloy processed by AM has not been investigated. Thus, in the present work, it was studied the influence of Ti-6Al-4V ELI alloy processed by AM on the wear resistance and morphologic of the coating obtained by PEO (plasma electrolytic oxidation). In this way, three different voltages (200, 250, and 300 V) were employed for the PEO process and the voltage effect on the properties of the coatings. The coatings were characterized by contact profilometry, scanning electron microscopy, energy-dispersive spectroscopy, the sessile drop method, grazing-incidence X-ray diffraction, and wear tests, on a ball-on-plate tribometer. The increase in applied voltage promoted an increase in roughness, pore area, and a decrease in the pore population of the coatings. In addition, the coatings, mainly composed of anatase and rutile, showed good adhesion to the metallic substrate, and the presence of bioactive elements Ca and P were detected. The thickness of the coatings obtained by PEO increases drastically for voltages higher than 250 V (from 4.50 ± 0.33 to 23.83 ± 1.5 µm). However, coatings obtained with lower voltages presented thin and dense layers, which promoted a superior wear resistance (increase in wear rate from 1.99 × 10⁻⁶ to 2.60 × 10⁻⁵ mm³/s). Finally, compared to the uncoated substrate, the PEO coatings increased the wear resistance of the titanium alloy obtained by AM, also showing a superior wear resistance compared to the commercial Ti-6Al-4V alloy previously evaluated, being such a positive and promising behavior for application in the area of metallic implants.

Hybrid films obtained by a sol-gel process are based on two important reactions: hydrolysis and condensation. The condensation reaction is influenced by the curing temperature, since it induces the development of the intrinsic properties of the gel. The aim of this work is to coat tinplate, a substrate widely used in the packaging industry, with monolayered and bilayered hybrid films modified with polyethylene glycol and obtained through dip-coating. The results showed that the bilayered hybrid film obtained at 60ºC had a higher layer thickness, and the best performance in the electrochemical assays, as well as the most hydrophobic character, in relation to the other samples. For the monolayered systems, the 90ºC-cured system showed a lower layer thickness; however, this system showed a more compact, uniform and less porous layer, and presented better electrochemical impedance results, in comparison with the 60ºC-cured samples.

The objective of this study was to evaluate the influence of sterilization on a hybrid coating obtained from a sol composed of alkoxysilane tetraethoxysilane (TEOS) and organoalkoxysilane methyltriethoxysilane (MTES) containing 10% (mass) of hydroxyapatite particles. The coating was obtained by dip coating, by applying two layers (protective/bioactive), which were cured at different temperatures (450°C and 60°C). The effects of sterilization on the superficial, electrochemical, bioactive, and mechanical properties of the coating were evaluated by performing different sterilization processes, namely, steam autoclave, hydrogen peroxide plasma, and ethylene oxide. Subsequently, the coating was characterized by using scanning electron microscopy (SEM/FEG), and FTIR measurements were performed to characterize the chemical structure. The bioactivity and degradability of the coating were analyzed by mass variation after immersion in SBF and X-ray diffraction (XRD) analysis. The electrochemical behavior was assessed by open circuit potential (OCP) and potentiodynamic polarization curves and the mechanical behavior by wear resistance. Results showed that all sterilization processes caused significant morphological changes in the hybrid coating. The autoclaved sample presented the highest structural chemical changes, and, consequently, the highest degradability, even though it had a superior bioactive behavior in relation to the other samples. In addition, the sterilization processes influenced the electrochemical behavior of the hybrid coating and altered the mechanical resistance to abrasion, thus presenting lower wear performance in relation to the nonsterilized sample.