We report here on soft-template electropolymerizations of polypyrrole (Ppy)-based nanocomposites triggered by graphene platelets (GP) from shungite (SH) rocks. A properly designed procedure for an efficient extraction of graphene platelets from SH powders is established to produce remarkable graphene materials in a low oxidation state and with a high electrical conductivity (1490 S cm⁻¹). By using positively and negatively charged templating surfactants the role played by the graphene units on the electropolymerization reactions is pointed out by SEM, EDX, TEM, SAED, XPS and Raman spectroscopy. The morphological/structural characterizations highlight that GP from SH have a surface chemistry suitable for selective and mutual interactions with the growing Ppy chains. CV and galvanostatic charge/discharge measurements evidence that GP improve the transport of both electrons and ions within the bulk material by means of a synergistic action with the polymer phase. This cooperative behavior induces an enhancement of the specific capacitance up to 250 F g⁻¹ at 2 A g⁻¹. The Ppy-GP materials produced following the settled protocols result to be appropriate for fabricating multifunctional charge transport and storage electroactive systems.

Designing fully green materials for flexible electronics is an urgent need due to the growing awareness of an environmental crisis. With the aim of developing a sustainable, printable, and biocompatible material to be exploited in flexible electronics, the rheological, structural and charge transport properties of water-based hydroxypropyl cellulose (HPC)-detonation nanodiamond (DND) viscous dispersions are investigated. A rheological investigation disclosed that the presence of the DND affects the orientation and entanglement of cellulose chains in the aqueous medium. In line with rheological analyses, the NMR diffusion experiments pointed out that the presence of DND modifies the hydrodynamic behavior of the cellulose molecules. Despite the increased rigidity of the system, the presence of DND slightly enhances the ionic conductivity of the dispersion, suggesting a modification in the charge transport properties of the material. The electrochemical analyses, performed through Cyclic Voltammetry (CV) and Electrochemical Impedance Spectroscopy (EIS), revealed that the HPC-DND system is remarkably stable in the explored voltage range (−0.1 to +0.4 V) and characterized by a lowered bulk resistance with respect to HPC. Such features, coupled with the printability and filmability of the material, represent good requirements for the exploitation of such systems in flexible electronic applications.