In this paper, surface projection micron stereo-lithography technology (PμSL) by 3D printing was used to prepare two resin honeycomb materials with different levels, and the mechanical behavior of these materials was studied. The quasi-static compression experiment and the dynamic compression experiment were carried out on the samples using the in situ micro-compression testing machine and the Split Hopkinson bar (SHPB) experimental equipment. The stress–strain curves of these materials at different strain rates were obtained, and the energy absorption characteristic of materials with two different levels were analyzed. This article reveals that the collapse strength and energy absorption properties of the materials are related to the hierarchical level of honeycomb. Multi-level hierarchical honeycomb (MHH) has higher collapse strength and better energy absorption properties than single-level hierarchical honeycomb (SHH). It turned out that increasing the hierarchical level of honeycomb could improve the mechanical properties of the materials. In the future development of products, the mechanical properties of hierarchical material by 3D printing can be further optimized through changing the level of the fractal structure.

The elastoplastic properties of TiC particle-reinforced titanium matrix composites (TiC/TMCs) at high temperatures were examined by quasi-static tensile experiments. The specimens were stretched at 300 °C, 560 °C, and 650 °C, respectively at a strain rate of 0.001/s. scanning electron microscope (SEM) observation was carried out to reveal the microstructure of each specimen tested at different temperatures. The mechanical behavior of TiC/TMCs was analyzed by considering interfacial debonding afterwards. Based on Eshelby’s equivalent inclusion theory and Mori-Tanaka’s concept of average stress in the matrix, the stress or strain of the matrix, the particles, and the effective stiffness tensor of the composite were derived under prescribed traction boundary conditions at high temperatures. The plastic strains due to the thermal mismatch between the matrix and the reinforced particles were considered as eigenstrains. The interfacial debonding was calculated by the tensile strength of the particles and debonding probability was described by Weibull distribution. Finally, a meso-mechanical constitutive model was presented to explore the high-temperature elastoplastic properties of the spherical particle-reinforced titanium matrix composites by using a secant modulus method for the interfacial debonding.