Objective: To evaluate the effects of different polishing techniques and coffee staining on the color stability of four commercially available bleach-shade composite resins, namely microhybrid, nanohybrid, nanofilled, and injectable nanohybrids. Material and methods: A total of 224 discs (8 mm diameter and 2 mm thickness) were fabricated from four different bleach-shade composite resins, namely microhybrid (Gradia Direct Anterior), nanohybrid (Palfique LX5), nanofilled (Filtek Universal), and injectable nanohybrid (flowable G-aenial universal injectable). The composite resin groups were polished via four techniques: no polishing, 4-step polishing using aluminum oxide discs, 3-step polishing using silicon rubber diamond discs, and one-step polishing. Half of each group was immersed in water, while the other half was immersed in coffee for 12 days (n = 7). Colors were measured using a clinical spectrophotometer, and color differences were calculated (ΔE). The results were analyzed statistically. Results: The alterations in color were significantly influenced by the techniques employed for finishing and polishing techniques, composite resin type, and degree of coffee staining. Regardless of the polishing technique and storage medium, different material types showed a significant color change (ΔE) at P < 0.001. Filtek exhibited the most significant color change, followed by Gradia and Palfique, with no significant differences between them. In addition, Different polishing techniques resulted in significant color changes (P < 0.001). The highest degree of color change was seen in the no-polishing group, followed by the 4-step and 1-step polishing groups, with negligible differences between each other. Also, Storage media had a significant effect on ΔE values. Conclusion: Appropriate finishing and polishing procedures can improve the color stability of bleach-shaded composite resins. Coffee has a deleterious effect on color; however, injectable flowable nanohybrid composites are more resistant to staining.

This study aimed to evaluate and compare the fatigue resistance of ProTaper Gold (PTG) and ProTaper Universal (PTU) in artificial single and double curvature canals in 5% sodium hypochlorite (NaOCl) at body temperature (37 °C). PTG and PTU files (size F1) were subjected to fatigue tests in two different artificial ceramic canals. The single curvature model had a 60° curvature angle with a 5 mm radius. The double curvature model had a 60° curvature angle with a 5 mm radius and a second 30° curvature with a 2 mm radius. A file segment was introduced into the artificial canal and immersed in water or 5% NaOCl at 37 °C. The total number of cycles to fracture (NCF) was recorded. Data were analyzed using t-test and linear regression analysis. The NCF of all files was significantly influenced by the type of NiTi metal alloy (P < .01), canal curvatures (P < .01), and the environmental conditions (P < .05). PTG had higher fatigue resistance than PTU files in both single and double curvature canals (P < .05). The NCF of PTU files in 5% NaOCl was shorter than that in water (P < .05). The mean length of broken PTG was significantly shorter than those of PTU files in both single and double curvature canals (P < .01). The fatigue performance of PTG is better than that of PTU in both single and double curvature. Environmental conditions may affect the fatigue behavior of PTU files with single curvature.

Background: This in vitro investigation aimed to determine the influence of multiple autoclave cycles on the cyclic fatigue resistance of three heat-treated nickel-titanium (NiTi) files: EdgeTaper Platinum (ETP), ProTaper Gold (PTG), and TruNatomy Prime (TN). Materials: Sixty NiTi files, twenty of each NiTi file type: ETP 25/.06, PTG 25/.08, and TN 26/.04 were randomly divided into four equal subgroups (n = 5). The files for the control group were left un-autoclaved. Different autoclave sterilization cycles (one, five, and ten) were used for the other three groups. The files were then placed in a metal canal block and rotated according to the manufacturer’s instructions until fracture. The length of the broken segment and the time taken for fracture were measured. The fractured surfaces were subsequently subjected to SEM imaging. The Kruskal-Wallis test was used to analyze the data, followed by Dunn-Bonferroni pairwise comparisons. Statistical significance was set at p < 0.05. Results: ETP showed significantly greater resistance to cyclic fatigue than TN in all autoclave groups and PTG after five autoclave cycles (p = 0.014). Fatigue resistance was not affected by the number of autoclaving cycles, except for ETP. After the first and tenth autoclaving cycles, they required significantly more rotations to failure than the non-sterilized files (p = 0.039 and p = 0.021, respectively). The fractured segments of the ETP files in these two groups were also longer than those in the control group (p = 0.010). Conclusion: The cyclic fatigue resistance of ETP was greater than that of TN in all tested conditions. Repeated autoclave cycles of sterilization improved the cyclic fatigue resistance of the ETP files only and did not affect the cyclic fatigue resistance of TN and PTG. However, the ETP files separated at a longer distance from the tip with increased autoclaving cycles.

Background and Objectives. The aim of this study is to explore the current state of endodontic practical training in Saudi dental schools and its relevance to contemporary endodontic practice. Materials and Methods. An online questionnaire was developed and emailed to all dental schools in Saudi Arabia. This questionnaire was answered by the endodontic undergraduate program director. The data collected were analysed using descriptive statistics. Results. The response rate was 96.15, which means twenty-five out of twenty-six dental schools participated in the study. The majority of the academic supervisors was endodontists (92). The use of magnification and ultrasonic tips was not required by 84 and 76 of the dental schools, respectively. The main endodontic treatment techniques were the step-back technique and gates glidden for cleaning and shaping (76) and cold lateral compaction for obturation (92). Conclusions. The dental students were supervised by endodontic specialists and trained to use traditional endodontic methods. Encouraging dental educators to train students to use modern technology and equipment would probably improve their graduate clinical skills and performance.

Introduction. Coronal leakage is detrimental to the long-term success of root canal treatment (RCT). While much emphasis is being placed on the quality of the final restoration, little attention is given to the temporary restoration placed in between root canal treatment appointments. The aim of this study was to survey temporization techniques practiced in Saudi Arabia and the frequency of observing temporary material breakdown or complete loss. Materials and Methods. An online questionnaire was distributed among general dentists, dental specialists, and clinical trainees in undergraduate and postgraduate dental programs. The sample size was estimated at 370 participants. Data were analyzed using descriptive statistics and chi-square tests. Results. The total number of participants who met the inclusion criteria was 525. The majority of them (94.6) were practicing two-visit RCT. The most common temporization materials were Cavit (50.3) followed by glass ionomer cement (32). The majority (72.6) of participants claimed they allow a thickness of 2-3mm for temporary restorations. Many participants (60.4) used a spacer material during temporization, and the cotton pellet was the most common spacer material. Temporary restoration breakdown or complete loss was a common observation. Although the duration between the two RCT visits was 2 weeks or less for 83.6 of participants, only 19.6 of participants claimed that they rarely observed temporization breakdown. Conclusion. Two-visit RCT is commonly practiced in Saudi Arabia, and endodontists performed significantly more single-visit procedures. Temporization practices may lack uniformity; however, clinicians were more likely to use calcium sulfate-derived material for two weeks or less. They allow for 2-3mm thickness restoration and use a cotton pellet as a spacer. According to their clinical observation, temporary material breakdown or complete loss was frequent. This mandates further attention in research and education.

The objective was to evaluate the effect of glide path and coronal flaring on the dentin volume removal and percentage of touched walls in curved canals using two heat-treated rotary files. The mesiobuccal canal of forty-eight, randomly selected, extracted mandibular molars was divided into two groups of 24 each, according to the type of instrument used (RACE EVO and EdgeSequel rotary files). Each group was further divided into three subgroups; Group (A): Control using one file shaped to 04/30, Group (B) with a glide path (EdgeGlidePath (EGP)), and Group (C): with a glide path and coronal flaring (EGP and EdgeTaper Platinum (ETP) SX file respectively). The root canals were then instrumented using the assigned instruments. The assessment was carried out using micro-CT. The comparison of the mean values of the tested groups about dentin volume removal and percentage of untouched walls did not reach statistical significance (p<0.05). Glide path and coronal flaring had an insignificant effect on the dentin volume removal and percentage of untouched walls in curved canals.