In this paper we report the crystal growth conditions and optical anisotropy properties of Tungsten ditelluride (WTe₂) single crystals. The chemical vapor transport (CVT) method was used for the synthesis of large WTe₂ crystals with high crystallinity and surface quality. These were structurally and morphologically characterized by means of X-ray diffraction, optical profilometry and Raman spectroscopy. Through spectroscopic ellipsometry analysis, based on the Tauc–Lorentz model, we identified a high refractive index value (~4) and distinct tri-axial anisotropic behavior of the optical constants, which opens prospects for surface plasmon activity, revealed by the dielectric function. The anisotropic physical nature of WTe₂ shows practical potential for low-loss light modulation at the 2D nanoscale level.

The electron-beam cycling additive technique was proposed for the formation of shape memory Ti-Ta coatings on titanium substrate. On a commercially pure Ti plate, Ta film with a thickness of about 4 μm was deposited by direct current (DC) magnetron sputtering. The sample was then subjected to an electron-beam surface alloying by a scanning electron beam. On the already-formed Ti-Ta surface alloy, a Ta coating with the same thickness was further deposited and the specimen was again subjected to electron-beam alloying for the second cycle. The same procedure was repeated for the third cycle. The structure obtained after each cycle Ti-Ta coatings was studied by X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM), and Energy-dispersive X-ray spectroscopy (EDX). The Young’s modulus, hardness, and shape memory effect (SME) were studied by nanoindentation experiments. The results showed that the thickness of the Ti-Ta coatings is about 50 μm in all cases, where the Ta content increases after each technological cycle. It was found that the obtained phase composition is in the form of a double-phase structure of α’ martensitic and β phases, where the highest amount of beta is registered in the case of the Ti-Ta coating obtained after the third cycle. The results obtained for the Young’s modulus and hardness showed that both mechanical characteristics decrease significantly after each cycle. Additionally, the elastic depth recovery ratio increases with an increase in the number of cycles.

Recently, low-dimensional structures in the form of bulk crystals and nanoflakes have received considerable interest due to their 2D unique functionality and promising applications in electronics, photonics, sensing devices and photovoltaic solar cells. As a result, remarkable efforts and modifications have been made for the synthesis process of crystalline material by the vapor transport technique. Here, an alternative concept of NbSe₂ crystal growth by the chemical vapor transport (CVT) technique using bromine as a vapor transport agent is presented and subsequently analyzed by X-ray diffraction (XRD), Raman and X-ray photoelectron spectroscopy (XPS) spectroscopy. X-ray powder diffraction analysis revealed hexagonal 2H-NbSe₂ and 4H-NbSe₂ phases, and characteristic Raman and XPS spectra typical for crystalline NbSe₂ were obtained. The environmental sensitivity of the grown crystals is manifested by luminescence attributed to oxidized Nb at the samples’ surface.