In the processing of thermoplastic composites, great importance is attributed to the consolidation step, as it can significantly reduce the porosity of the semi-finished product and thus influence considerably the quality of the final component. This work presents an approach to modeling the thermodynamic behavior of composite materials during hot-press consolidation. For this purpose a multi-region, multi-phase and multi-component-mixture model was developed using the simulation toolbox OpenFOAM^®. The sensitivity of the model was tested by varying the thermal parameters and mesh resolution, confirming its robustness. Validity of the model was confirmed by comparing simulation results to experimental data for (i) polycarbonate with 44% carbon fiber by volume and (ii) polypropylene with 45.3% glass fiber by volume. The simulation allows very precise estimation of when a particular temperature, such as the glass transition temperature or melting point, will be reached at the core of a composite. In relation to the total process time, maximum deviation of the simulation from the experimental data amounted to 2.84%. Therefore, the model is well suited for process optimization, it offers a basis for further model implementations and the creation of a digital twin.

The aim of this work was to optimize spot welding of unidirectional tapes made of polycarbonate and carbon fibers. Three studies were performed to investigate the influences of various welding conditions on the quality of the welded spot. First, we used a full factorial experimental design to analyze the influence of temperature and time on the welds’ tensile stress at break. Second, we repeated the experiment with optimized settings and conditions. Finally, we adopted a central composite design (CCD) to investigate the stability of the process. Our results show that temperature had the greatest influence on weld quality. The maximum tensile stress achieved was 23 MPa. Using a relatively high temperature for a short welding time resulted in self-cleaning of the welding head and in a faster and more stable process, and gel permeation chromatography (GPC) confirmed that these conditions caused no additional degradation.

The main aim of this work was to optimize the consolidation of unidirectional fiber-reinforced thermoplastic composite tapes made of polycarbonate and carbon fibers using a heating press and a cooling press in combination. Two comprehensive studies were carried out to investigate the impact of process settings and conditions on the quality of the consolidated parts. The initial screening study provided valuable insights that informed the design of the second study, in which the experimental design was expanded and various modifications, including the implementation of a frame tool, were introduced. The second study demonstrated that the modifications in combination with a high heating press temperature and elevated heating and cooling pressures successfully achieved the desired goals: the desired thickness (2 mm), improved bonding strength (23% increase), and reduced void content (down to 4.64%) in the consolidated parts.

The anisotropic material behavior of continuous-fiber-reinforced composites that is evident in their mechanical properties should also be considered in their processing. An important step in the processing of thermoplastic unidirectional (UD) fiber-reinforced tapes is consolidation, where a layup consisting of locally welded UD tape layers is firmly bonded. Compression of the molten thermoplastic matrix material during consolidation leads to a squeeze flow, the direction of which is determined by the fibers. This work presents a model that describes the influence of fiber direction on compression and flow behavior, implemented in the computational fluid dynamics (CFD) software tool OpenFOAM^®. To validate the simulation results, we performed experiments in a laboratory consolidation unit, capturing the squeeze flow with cameras and then quantifying it by gray-scale analysis. The specimens used were UD polycarbonate tapes (44% carbon fibers by volume) of various sizes and with various fiber directions. The simulation allows prediction of the changes in specimen geometry during consolidation and is a first step towards optimizing the process by avoiding extensive squeeze flow.

In the processing of thermoplastic composites, joining UD tapes to form a layup is a crucial step. In the pick- and-place approach, multiple tapes are spot-weld In the processing of thermoplastic composites, joining UD tapes to form a layup is a crucial step. In the pick- and-place approach, multiple tapes are spot-weld

Consolidation is an important step in the processing of thermoplastic unidirectional (UD) tapes, as it creates a bond between individual tapes to form a semi-finished sheet: The tape stack is first heated and then cooled, both while being subjected to pressure. If the material is in a soft or even molten state and its flow unrestricted, this compression can result in squeeze flow, the direction of which is determined by the fibers of the tapes. Extensive squeeze flow not only results in significant changes in part geometry to the point where it may fail to meet design and application specifications but can also lead to severe distortion and residual stresses. To address this, we developed a model that, given the process parameters and fiber orientation, predicts the effects of squeeze flow. Based on experimental data on UD polycarbonate tapes with 44% carbon fibers by volume consolidated at various process settings, this paper presents the validation of the model for industrial application. We found that at low heating temperatures, where the matrix viscosity is too high and prevents the material from flowing, the simulation results deviated markedly from the experimental data. With these temperatures excluded, however, the overall deviation of the model was 8.7% for thickness change and 5.3% for area change.