We herein report on the preparation of epoxy nanocomposites, which had enhanced thermal conductivities but were still electrical insulators, incorporating hybrid nanosheets (NSs) with sandwich structures composed of thermally reduced graphene oxide (TRGO) and silica. The silica layer covered the surface of the TRGO, hindering electrical conduction and effectively forming a 3D phonon transport channel that had a unique effect on the electrical and thermal properties of the epoxy matrix. A 1 wt% TRGO–silica NS epoxy nanocomposite maintained an electrical resistivity of 2.96 × 10¹¹ Ω cm, and its thermal conductivity was 0.322 W m⁻¹ K⁻¹, which is 61% higher than the conductivity of an epoxy nanocomposite without TRGO–silica NSs (0.2 W m⁻¹ K⁻¹).

In this study, we reported the synthesis of the two-dimensional (2D) nanocomposite of molybdenum disulfide and nitrogen-doped graphene oxide (MoS2/nGO) as a platinum-free counter electrode (CE) for dye-sensitized solar cells (DSSCs). X-ray photoelectron spectroscopy (XPS), high-resolution transmission electron microscopy (HRTEM), and Raman spectroscopy were used to examine the characteristics of the 2D nanocomposite of MoS2/nGO. The cyclic voltammetry (CV), electrochemical impedance spectra (EIS), and the Tafel polarization measurements were carried out to examine the electrocatalytic abilities. XPS and Raman results showed the 2D behaviors of the prepared nanomaterials. HRTEM micrographs showed the direct evidence of the 2D nanocomposite of MoS2/nGO. The results of electrocatalytic examinations indicated the MoS2/nGO owning the low charge transfer resistance, high electrocatalytic activity, and fast reaction kinetics for the reduction of triiodide to iodide on the electrolyte–electrode interface. The 2D nanocomposite of MoS2/nGO combined the advantages of the high specific surface of nGO and the plenty edge sites of MoS2 and showed the promoted properties different from those of their individual constituents to create a new outstanding property. The DSSC with MoS2/nGO nanocomposite CE showed a photovoltaic conversion efficiency (PCE) of 5.95 % under an illumination of AM 1.5 (100 mW/cm2), which was up to 92.2 % of the DSSC with the conventional platinum (Pt) CE (PCE = 6.43 %). These results reveal the potential of the MoS2/nGO nanocomposite in the use of low-cost, scalable, and efficient Pt-free CEs for DSSCs.

A two-dimensional nanostructure of molybdenum disulfide (MoS2) thin film exposed layered nanosheet was prepared by a low-temperature thermally reduced (TR) method on a fluorine-doped tin oxide (FTO) glass substrate as a platinum (Pt)-free and highly electrocatalytic counter electrode (CE) for dye-sensitized solar cells (DSSCs). Thermogravimetric analysis (TGA) results show that the MoS2 sulfidization temperature was approximately 300 °C. X-ray photoelectron spectroscopy (XPS), high-resolution transmission electron microscopy (HRTEM), and X-ray diffraction (XRD) indicate that the stoichiometry and crystallization of MoS2 were more complete at higher temperatures; however, these temperatures reduce the number of edge-plane active sites in the short-range-order nanostructure. Accordingly, the DSSCs with 300 °C annealed TR-MoS2 CE exhibited an excellent photovoltaic conversion efficiency (PCE) of 6.351 %, up to 91.7 % of which is obtained using the conventional TD-Pt CE (PCE = 6.929 %). The temperature of thermal reaction and the molar ratio of reaction precursors were found to significantly influence the resulting stoichiometry and crystallization of MoS2 nanosheets, thus affecting DSSCs’ performance.