This study aimed at evaluating the microtensile bond strength (MTBS) and fractographic features of dentine-bonded specimens created using universal adhesives applied in etch-and-rinse (ER) or self-etching (SE) mode in combination with modern ion-releasing resin-modified glass-ionomer cement (RMGIC)-based materials after load cycling and artificial saliva aging. Two universal adhesives (FTB: Futurabond M+, VOCO, Germany; SCU: Scotchbond Universal, 3M Oral Care, USA) were used. Composite build-ups were made with conventional nano-filled composite (AURA, SDI, Australia), conventional resin-modified glass ionomer cement (Ionolux VOCO, Germany), or a (RMGIC)-based composite (ACTIVA, Pulpdent, USA). The specimens were divided in three groups and immersed in deionized water for 24 h, load-cycled (350,000 cycles; 3 Hz; 70 N), or load-cycled and cut into matchsticks and finally immersed for 8 months in artificial saliva (AS). The specimens were cut into matchsticks and tested for microtensile bond strength. The results were analyzed statistically using three-way ANOVA and Fisher’s LSD post hoc test (p < 0.05). Fractographic analysis was performed through stereomicroscope and FE-SEM. FTB showed no significant drop in bond strength after aging. Unlike the conventional composite, the two RMGIC-based materials caused no bond strength reduction in SCU after load-cycle aging and after prolonged aging (8 months). The SEM fractographic analysis showed severe degradation, especially with composite applied on dentine bonded with SCU in ER mode; such degradation was less evident with the two GIC-based materials. The dentine-bond longevity may be influenced by the composition rather than the mode of application (ER vs. SE) of the universal adhesives. Moreover, the choice of the restorative material may play an important role on the longevity of the finalrestoration. Indeed, bioactive GIC-based materials may contribute to maintain the bonding performance of simplified universal adhesives over time, especially when these bonding systems are applied in ER mode.

This study aimed at evaluating the efficacy of a novel silver-citrate root canal irrigation solution (BioAKT) on smear layer removal, sealer penetration after root canal instrumentation and antibacterial activity. Single-root teeth were endodontically treated, sealed with an epoxi-amine resin sealer and irrigated using: Group I: 5.25% sodium hypochlorite (NaOCl); Group II: silver-citrate solution (BioAKT); Group III: phosphate buffer solution (PBS); Group IV: 17% ethylenediaminetetraacetic acid (EDTA). Smear layer removal and silver deposition at the coronal, middle and apical portion of each canal were analyzed using scanning electron microscopy (SEM) and energy-dispersive x-ray spectroscopy (EDS). Sealer penetration into dentinal tubules at coronal, middle and apical portion was assessed through dye-assisted confocal microscopy (CSM). Both SEM and CSM micrographs were evaluated by two examiners (κ = 0.86), who were blind to the irrigation regimens; scores were given according to the degree of penetration of the sealer. Data analysis included Pearson’s x² and Sidak’s multiple comparisons. Dentin discs were polished and sterilized. Enterococcus faecalis biofilms were grown using a continuous-flow bioreactor under anaerobic conditions for 72 h. Specimens were irrigated with the tested solutions, and bacterial viability was assessed using a tetrazolium salt assay (MTT). Statistical analysis included one-way ANOVA and Student’s post-hoc t-test (p < 0.05). BioAKT and EDTA were the most efficient solutions both in removing the smear layer and allowing sealer penetration. However, at the apical portion BioAKT performed significantly better compared to EDTA both in smear layer removal and sealer penetration (p < 0.05). BioAKT and NaOCl showed comparable antibacterial effect (p = 0.53). In conclusion, BioAKT represents a suitable smear layer removal agent, which allows for reliable sealer penetration at the apical portion of the root canal system and offers significant antibacterial properties.

To evaluate the biomodification ability of lignin used as pre-treatment in human dentin before the application of an etch-and-rinse adhesive. Experimental hydroethanolic solutions with different cross-linking agents were used: 6.5% proanthocyanidins (PAC, from grape-seed extract); 2% cardanol (CARD, from cashew-nut shell liquid); lignin (LIG, from eucalyptus) at 1, 2 or 4% concentrations. The negative control (NC) was ethanol 50 v%. Extracted molars were prepared, and dentin microtensile bond strength (μTBS) was evaluated after 24 h water storage or 10,000 thermocycling aging. Further specimens were processed for SEM nanoleakage, micropermeability confocal microscopy evaluation and in situ degree of conversion (DC) through micro-Raman spectroscopy. Demineralized dentin sticks were submitted to a three-point bending test to evaluate the elastic modulus (E) before and after 1 min biomodification using the tested solutions. Moreover, it was also evaluated the mass changes and hydroxyproline (HYP) release after 4-weeks of water storage. Vibrational collagen crosslinking identification was evaluated through micro-Raman spectroscopy. The results were analyzed by analysis of variance (ANOVA) and Tukey’s test (α = 0.05). A significant reduction in μTBS was observed in groups NC (p < 0.001) and CARD (p = 0.026). LIG-4% showed no significant reduction in μTBS after aging (p = 0.022). Nanoleakage micrographs showed hybrid layer protection with all agents, but reduced micropermeability was attained only with lignin. Polymerization was negatively affected in the presence of all tested cross-linking agents, except LIG-1%. Lignin and cardanol increased the dentin E values, but only lignin reduced the mass loss in dentin specimens. Effective collagen crosslinking (1117 cm⁻¹ and 1235 cm⁻¹) was detected for all agents. HYP release was significantly lower with LIG-1% than NC (p < 0.001). Lignin was able to perform collagen cross-linking and prevent the degradation of unprotected dentin collagen, thereby improving the bonding performance of the composite restorations performed in this study.