Magnetite nanoparticles were synthesized by the co-precipitation method with and without the assistance of an additive, namely, gelatin, agar-agar or pectin, using eco-friendly conditions and materials embodying a green synthesis process. X-ray diffraction and transmission electron microscopy were used to analyze the structure and morphology of the nanoparticles. Magnetic properties were investigated by SQUID magnetometry and ⁵⁷Fe Mössbauer spectroscopy. The results show that the presence of the additives implies a higher reproducibility of the morphological magnetic nanoparticle characteristics compared with synthesis without any additive, with small differences associated with different additives. To assess their potential for magnetic hyperthermia, water-based suspensions of these nanoparticles were prepared with and without citric acid. The stable solutions obtained were studied for their structural, magnetic and heating efficiency properties. The results indicate that the best additive for the stabilization of a water-based emulsion and better heating efficiency is pectin or a combination of pectin and agar-agar, attaining an intrinsic loss power of 3.6 nWg⁻¹.

Magnetic fluid hyperthermia, a minimally invasive localized therapy that uses heat generated by magnetic nanoparticles under an AC magnetic field, is a complementary approach for cancer treatment that is excellent due to its advantages of being noninvasive and addressing only the affected region. Still, its use as a stand-alone therapy is hindered by the simultaneous requirement of nanoparticle biocompatibility, good heating efficiency, and physiological safe dose. To overcome these limits, the biocompatible magnetic nanoparticles’ heating efficiency must be optimized. Iron oxide nanoparticles are accepted as the more biocompatible magnetic nanoparticles available. Therefore, in this work, superparamagnetic iron oxide nanoparticles were synthesized by a low-cost coprecipitation method and modified with starch and gum to increase their heating efficiency and compatibility with living tissues. Two different reducing agents, sodium hydroxide (NaOH) and ammonium hydroxide (NH₄OH), were used to compare their influence. The X-ray diffraction results indicate the formation of a single magnetite/maghemite phase in all cases, with the particle size distribution depending on the coating and reducing agent. Citric acid functionalized water-based ferrofluids were also prepared to study the heating efficiency of the nanoparticles under a magnetic field with a 274 kHz frequency and a 14 kAm⁻¹ amplitude. The samples prepared with NaOH display a higher specific loss power (SLP) compared to the ones prepared with NH₄OH. The SLP value of 72 Wg⁻¹ for the magnetic nanoparticles coated with a combination of starch and gum arabic, corresponding to an intrinsic loss power (ILP) of 2.60 nWg⁻¹, indicates that they are potential materials for magnetic hyperthermia therapy.